Search

In this paper, an accurate formula for calculating the thermal residual stress field in a particle-reinforced composite are presented. Numerical examples are given to show r-variations of the thermal residual stresses. The increase in fracture toughness of matrix predicted by the thermal residual stress field is compared well with the experimentally measured increase. [ABSTRACT FROM AUTHOR]

The fracture process of composite laminates subjected to static or fatigue tensile loading involves sequential accumulation of intra- and interlaminar damage, in the form of transverse cracking, splitting and delamination, prior to catastrophic failure. Matrix cracking parallel to the fibres in the off-axis plies is the first damage mode observed. Since a damaged lamina within the laminate retains certain amount of its load-carrying capacity, it is important to predict accurately the stiffness properties of the laminate as a function of damage as well as progression of damage with the strain state. In this paper, theoretical modelling of matrix cracking in the off-axis plies of unbalanced symmetric composite laminates subjected to in-plane tensile loading is presented and discussed. A 2-D shear-lag analysis is used to determine ply stresses in a representative segment and the equivalent laminate concept is applied to derive expressions for Mode I, Mode II and the total strain energy release rate associated with off-axis ply cracking. Dependence of the degraded stiffness properties and strain energy release rates on the crack density and ply orientation angle is examined for glass/epoxy laminates. Suitability of a mixed mode fracture criterion to predict the cracking onset strain is also discussed. [ABSTRACT FROM AUTHOR]

The effect of static and cyclic loading conditions on the stress corrosion cracking of unidirectional glass reinforced polymer (GRP) rods used in composite high voltage insulator has been investigated. A series of stress corrosion experiments have been performed on unidirectional E-glass/modified polyester composite rods. The rods have been subjected to mechanical tensile static and cyclic stresses in the presence of a nitric acid solution. The stress corrosion fracture process in the rods was monitored using acoustic emission techniques. The experimental loading conditions simulated possible in-service loadis for composite suspension insulators. The results obtained in this study showed that the brittle fracture process can be generated in the rods when subjected to relatively low tensile stresses in the presence of a nitric acid solution. The morphology of the experimentally generated brittle fracture cracks in the rods closely resemble those from in-service failed composite suspension. It has also been shown in this research that low frequency, low amplitude vibrations in tensile loads can significantly accelerate the fracture process. It appears that the brittle fracture cracks in the rods generated under cyclic loads are less planar in nature in comparison with the cracks formed under static conditions. It has also been found that the acoustic emission generated during the stress corrosion fracture process in the rods is sensitive to the placement of the transducers. However, reasonably good correlation between the stress corrosion crack growth rates and acoustic emission has been attained. [ABSTRACT FROM AUTHOR]