In this paper, copper coated carbon nanotubes (CNTs) was synthesized by decomposition of Cu(II) acetylacetonate (Cu(acac)2) in hydrogen atmosphere at 300 °C. The thickness of the copper coating was in nanoscale according to scanning electron microscopy (SEM) and transmission electron microscopy (TEM) images, and Raman spectra indicated that certain intermediate bonds were formed between copper and the template CNTs. The crystalline structure of copper and its growth orientation were determined by X-ray diffraction (XRD) and selected area electron diffraction (SAED). The copper coating on CNTs had a face-centered cubic structure and its growth orientation was parallel to $$ (\bar 111) $$ planes. The method developed in this paper had the advantages of simplicity in both process control and experiment equipments, so that it might provide a possibility of large-scale production. [ABSTRACT FROM AUTHOR]

Gd3+ was chosen as a substitute for Bi3+ in BiNbO4 ceramics, and the substitution effects on the sintering performance and microwave dielectric properties were studied in this paper. The high temperature triclinic phase was observed only in the Bi0.98Gd0.02NbO4 ceramics when sintered at 920 °C. Both bulk densities and dielectric constant (εr) increased with the sintering temperature, while decreased with the Gd content. The quality factor ( Q) exhibited a correlation to the Gd content and the microstructures of Bi1− x Gd x NbO4 ceramics. At the sintering temperature of 900 °C, Bi0.992Gd0.008NbO4 ceramics exhibited microwave dielectric properties of εr ∼ 43.87, Q × f ∼ 16,852 GHz (at 4.3 GHz), and its temperature coefficient of resonant frequency (τf) was found to be near-to-zero. [ABSTRACT FROM AUTHOR]

Cuprous oxide (Cu2O) nano- and microstructures possess unique properties that may find a variety of applications. Environmentally benign synthesis of Cu2O with well-controlled morphology is highly desirable. In this study, Cu2O crystals with tunable shapes are synthesized using cellulose nanofibrils (CNFs) as a shape regulator and the sole reducing agent in aqueous environment. By simply increasing Cu2O precursor concentration, the Cu2O crystals evolved from octahedra to cuboctahedra, and finally cubes, accompanied with increasing size from nano- to microscale. The selection of Cu chelating agent (sodium tartrate or potassium sodium tartrate) affected the crystal growth rate. Transition in the relative intensities of the (111) and the (200) crystalline peaks in their XRD patterns was consistent with the morphology change. During the growth of crystals, CNFs were preferably bound to the {111} crystalline facet. The introduction of KBr to the reaction system produced short hexapods. The resultant CNF-Cu2O hybrids were incorporated into waterborne polyurethane (WPU) films. Even with 0.5 wt% CNF-Cu2O, the WPU film showed significant enhancement in modulus, strength and elongation at break. This work proves the possibility of controlled growth of Cu2O particles aided by CNFs and provides a new strategy for improving the performance of eco-friendly WPU films. [ABSTRACT FROM AUTHOR]