Mechanical properties of Ti/Al–7Si assemblies produced by insert moulding were studied with a classical push-out test and a variant that is the circular-bending test. Special care has been taken for controlling both the reactivity at the Ti/Al–7Si interface and the metallurgical health of the Al–7Si matrix. Mechanical tests until complete debonding have been completed with interrupted tests, metallographic characterizations and FEM analysis of elastic stress state. A mean shear strength of the interface of about 120 MPa was obtained. When the Ti insert is solely fretted in the matrix, without chemical interaction between Ti and the Al–7Si alloy, the mean shear strength is significantly lower (48 MPa). This result clearly shows that chemical interaction at the interface (formation of a thin TiSi layer at the Ti side and a thick Al3Ti(Si) layer at the Al–7Si alloy side) improves the mechanical properties of the assembly. It is also shown that the failure sequence is characterized both by crack propagation from bottom to top and matrix yielding from top to bottom. Actually, interface damaging begins by crack initiation at the specimen bottom face (not at the top face and under the indenter) in a nearly pure mode I solicitation at a radial tensile stress of about 100 MPa. [ABSTRACT FROM AUTHOR]

A microstructural characterisation of the family of N-methyl-N-alkylpyrrolidinium tetrafluoroborate organic salts was carried out by observation of powder surface morphologies with the aim of extending the microstructure-property correlation. Inherent difficulties limiting extensive studies of organic solids by SEM, including volatility under vacuum, charging due to electron beam irradiation, and air-sensitivity were overcome with the use of a Field Emission SEM and cryostage attachment. This technique, providing considerable improvements in image quality at low accelerating voltages, enabled direct observation of complex microstructural features in samples exhibiting high temperature plastic crystalline phases (N,N-dimethylpyrrolidinium tetrafluoroborate [P11BF4]; N-methyl-N-ethylpyrrolidinium tetrafluoroborate [P12BF4]; N-methyl-N-propylpyrrolidinium tetrafluoroborate [P13BF4]). Extensive lattice imperfections including grain boundaries, slip planes and dislocation pits were observed within particles of approximately 200 μm diameter. The N-methyl-N-butylpyrrolidinium tetrafluoroborate (P14BF4) sample in this series revealed columnar single crystals with high aspect ratios. The origin of plastic flow properties is discussed using single crystal and polycrystalline slip observations and a relationship proposed between defect characteristics and transport properties. [ABSTRACT FROM AUTHOR]