Novel enzymatically hardened tetracalcium phosphate/monetite cements were prepared applying phytic acid/phytase (PHYT/F3P) mixture as hardening liquid after dissolving in acetic acid solution (CX cement). Properties of the cements were compared with classic cement hardened with 2% NaH2PO4 (C cement) and cement hardened with acetic acid solution (CAC cement) only. In the microstructure of CX cement, columnar growth of hydroxyapatite particles was found in the form of walls around hydroxyapatite agglomerates originated from tetracalcium phosphate which were mutually separated by a material depleted low density zone. Wet compressive strengths (CS) of all cements were practically identical contrary to about 30% higher dry CS's of CX and CAC cements due to specific microstructure. It was verified noncytotoxic character of CX cement extracts and positive effect of CX cement on ALP activity and cell behavior during cultivation. The final Ca/P molar ratio and setting time of cement were effectively controlled by the amount of phytic acid and the change in PHYT/F3P mass ratio, or reaction time in hardening liquid, respectively.

Biphasic porous calcium phosphate ceramics was prepared by sintering of transformed tetracalcium phosphate-monetite cement. After annealing hydroxyapatite, β- or α-TCP were found as main phases in ceramic substrates and a highly microporous microstructure of cement ceramics was created without an addition of porosifier. The origin microstructure features characteristic by the presence of hollow particle agglomerates in cement were preserved in microstructure of cement ceramics after annealing but the hydroxyapatite particles rose in size up to 2 µm and obtained a more regular shape. A small decrease in compressive strength was demonstrated in ceramics sintered up to 1150 °C and enhanced osteoblast proliferation was revealed on cement ceramic substrates in comparison with cement sample and conventional ceramics. The ALP activity of osteoblasts decreased with rise in sintering temperature. The prepared cement microporous ceramics could be utilized as carrier for antibiotics, drugs, growth factors, enzymes or other substances stimulating healing process.