Elemental reorganisation and oxidation state changes of key active sites in Co–Fe spinels are investigated by in situ X-ray photoemission spectroscopy (XPS) and operando X-ray absorption spectroscopy (XAS) under oxygen evolution operating conditions. The combination of the two techniques allows identifying both the surface and bulk modifications on the oxides and relating them to the activity loss during extended cycling. The results show that Co–Fe spinels experience a surface irreversible phase evolution under oxygen evolution reaction (OER) conditions, resulting in the formation of an amorphous layer composed of new stable Co(iii) and Fe(iii) species. Accelerated ageing tests show that the durability, intended as the performance loss during cycling treatments, is not directly related to the structural/chemical stability of the spinels but to the new species formed at the surface due to the electrochemical work. Thus, the material that experienced more significant changes was also the most durable one, demonstrating that the understanding of the chemical and/or structural evolution of the materials during the catalytic process can be the key for the design of highly active and stable catalysts. [ABSTRACT FROM AUTHOR]

FeCo2O4 and CoFe2O4 nanoparticles have been studied as oxygen carriers for the Chemical Loop Reforming (CLR) of ethanol. By using in operando X-ray absorption spectroscopy we have followed in real time the chemical and structural changes that take place on the materials as a function of temperature and reactive atmosphere (i.e. ethanol/water streams). During the first step of CLR for both oxides the most active chemical species are the cations in the tetrahedral sites, irrespective of their chemical nature. Quite rapidly the spinel structure is transformed into a mix of wüstite-type oxide and metal alloys, but the formation of a metal phase is easier in the case of cobalt, while iron shows a marked preference to form wüstite type oxide. Despite the good reducibility of FeCo2O4 imparted by the high amount of cobalt, its performance in the production of hydrogen is quite poor due to an inefficient oxidation by water steam, which is able to oxidize only the outer shell of the nanoparticles. In contrast, CoFe2O4 due to the residual presence of a reducible wüstite phase shows a higher hydrogen yield. Moreover, by combining the structural information provided by X-ray absorption spectroscopy with the analysis of the byproducts of ethanol decomposition we could infer that FeCo2O4 is more selective than CoFe2O4 for the selective dehydrogenation of ethanol to acetaldehyde because of the higher amount of Fe(iii) ions in tetrahedral sites. [ABSTRACT FROM AUTHOR]