Abstract: The polycrystalline samples of Bi1− x Nd x FeO3 (BNFO) with x=0, 0.05, 0.1, and 0.15 were prepared by a chemical route (metal ion complex precursor solution method). A systematic change in crystal structure from rhombohedral to tetragonal on increasing Nd substitution was observed. The reduction of low-frequency dispersion in permittivity and loss pattern due to Nd substitution in BiFeO3 (BFO) was observed in its dielectric response curve. The loss tangent (tan δ) was found to be reduced on increased Nd concentration in BNFO. Dielectric anomaly near the reported Neel temperature of BFO and peaks in all the BNFO samples were observed in the permittivity vs. temperature graph. Significant opening in the room temperature M–H loop was observed on Nd substitution, which was more prominent for higher concentration of Nd. [Copyright &y& Elsevier]

Highlights • Acrylamide polymer gel template method has been used to prepare single phase DyMnO 3. • Heat capacity measurement shows three transitions due to T N (Dy), T lock and T N (Mn). • Magnetic field strongly affect T N (Dy) and T lock as observed in heat capacity data. • The magnetic study reveals the presence of two transitions due to T N (Dy) and T lock. • Increase in weak ferromagnetic behaviour with decrease in temperature. Abstract Single phase polycrystalline DyMnO 3 (DMO) was synthesized using acrylamide polymer gel template method. We report the structural, magnetic, specific heat and dielectric properties of DMO over wide experimental conditions. Room temperature XRD pattern shows the formation of singe phase material without any impurity. The magnetic properties such as magnetization versus temperature (M vs. T) and magnetization versus magnetic field (M vs. H) were studied around the transition temperatures region. The temperature dependent magnetization data suggest two phase transitions corresponding to the lock-in temperature below which ferroelectric ordering exist (around 19 K; T lock) and antiferromagnetic (AFM) ordering of Dy spin (around 8 K; T N (Dy)). The magnetic hysteresis obtained were fitted to extract weak ferromagnetic (FM) and antiferromagnetic/paramagnetic (AFM/PM) contribution to the magnetic data. The order of magnetic transitions were analyzed from Arrott plot. The temperature dependent specific heat measurement shows all three phase transitions corresponding to (i) AFM ordering of Mn spin (around 38 K; T N (Mn)), (ii) T lock transition and (iii) T N (Dy) transition. The effect of magnetic field to the transitions were studied using specific heat capacity measurement. The peak intensity of T N (Dy) decreases on the application of magnetic field whereas peak intensity of T lock increases with increase in magnetic field in specific heat measurement. Further the third anomaly, T N (Mn) remains more or less unaffected by the application of magnetic field. The intrinsic dielectric behaviour of the material was observed up to 160 K, above this temperature there is large increase in dielectric value due to the contribution from Maxwell- Wagner polarization. [ABSTRACT FROM AUTHOR]