Search

To enhance mechanical, adhesive, and thermal properties of Room Temperature Vulcanized (RTV) silicone rubber, a silicon-containing polyurethane/epoxy resin modifier (ESiPU) was developed. A three-phase system of polyurethane/epoxy resin/silicone rubber was prepared through blending, modification, and co-curing. FT-IR and 1H-NMR were employed to characterize the chemical structure of ESiPU. Microscopic analysis revealed improved compatibility between modified epoxy resin and silicone rubber. Mechanical testing showed significant enhancements in tensile strength, elongation at break, and adhesive strength, with RTV-20phr exhibiting increases of 236, 266, and 259%, respectively. Thermogravimetric analysis indicated higher initial decomposition temperature compared to pure RTV. At the same time, the char residue at 800 °C increased to 8.67%. TG-IR analysis demonstrated ESiPU's ability to delay thermal degradation. Contact angle test confirmed improved hydrophobicity. Overall, the developed silicone rubber system exhibits promising mechanical and thermal properties, suggesting potential for aerospace heat protection applications. [ABSTRACT FROM AUTHOR]

A novel diphenyl monomer, dimethyl 2,2'-(((ethane-1,2-diylbis(oxy))bis(4-acetyl-3,1-phenylene))bis(oxy))diacetate (EDPD), was synthesized from methyl 2-(4-acetyl-3-hydroxyphenoxy)acetate (MAHA), a 2,4-dihydroxyacetophenonederivative, and combined with 1,4-butanediol, 1,6-hexanediol, 1,4-cyclohexanedimethanol or p-phenylenedimethanolto afford a series of biodegradable polyesters via melt polymerization. The polyesters were characterized by Fourier transform infrared and proton nuclear magnetic resonance spectroscopy, gel permeation chromatography, differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). The weight-average molecular weight (Mw) of the polyesters varied from 3.2–4.4 × 104 g/mol, the glass transition temperature (Tg) from 52 to 80 °C, and the 5% decomposition temperature (Td,5%) was in the 334–362 °C range. All the samples exhibited high yield strength (53–68 MPa) and elongation at break (230–330%) values, comparable with poly(ethylene terephthalate) (PET), owing to their aromatic character. Degradability testing of the polyesters in soil yielded mass losses reaching up to 7% after 32 weeks. In ecotoxicity testing, earthworms had a survival rate of more than 80% after 14 d of incubation, indicating relatively low toxicity. Overall, the good thermal and mechanical properties, biodegradability and low ecotoxicity of the polyesters make them promising materials for packaging applications, in replacement for PET, thereby promoting carbon neutrality and sustainable development. [ABSTRACT FROM AUTHOR]

Silicone resins are widely used in various fields because of their excellent high thermal stability. To improve their comprehensive performances, many organic resins have been used for modification of silicone resins. In this article, silicone resins containing phthalonitrile groups were synthesized by the reaction of the silicone resin containing amino groups and 4-(2-oxiranylmethoxy)-1,2-benzenedicarbonitrile. The structures of phthalonitrile-modified silicone resins were characterized by Fourier transform infrared spectroscopy (FT-IR) and nuclear magnetic resonance (1H-NMR). The curing process was characterized by differential scanning calorimetry and FT-IR. Thermogravimetric analysis results showed that the cured modified silicone resins had good thermal stabilities. Dynamic mechanical analysis indicated that they owned high glass transition temperature, suggesting that silicone resins containing phthalonitrile groups have high-temperature resistance. [ABSTRACT FROM AUTHOR]