Search

Recently discovered scintillators Cs 4 SrI 6 :Eu and Cs 4 CaI 6 :Eu have shown promising properties for gamma-ray detection in homeland security applications, with <4% energy resolution (at 662 keV) and light yields above 50,000 ph/MeV. However, a thorough investigation of the effects of europium concentration has not yet been conducted. In this work, Eu2+ concentration was varied from 0.5 mol% to 9 mol%, and Ø7 mm single crystals were grown from the melt via the vertical Bridgman method. Scintillation performance was evaluated as a function of Eu2+ concentration to determine the optimal amount. The observed trend was improved energy resolution and higher light yield with increasing Eu2+ concentration up to 7 mol%. The best energy resolution achieved was 3.2% for Cs 4 SrI 6 :Eu 7% and 3.6% for Cs 4 CaI 6 :Eu 7%. Their respective light yields were 71,000 ph/MeV and 69,000 ph/MeV. • Photoluminescence and radioluminescence emission show weak dependence on europium concentration in Cs4SrI6:Eu and Cs4CaI6:Eu. • A maximum light yield of 78,000 ph/MeV is obtained with 9 mol% europium in Cs4SrI6:Eu. • An energy resolution of 3.2% at 662 keV is achieved with 7 mol% europium in Cs4SrI6:Eu. [ABSTRACT FROM AUTHOR]

A self-activated Cs 4 YbI 6 single crystal was grown by the vertical Bridgman method. Crystal structure refinements verified the phase purity and the trigonal crystal system with a space group of R 3 ̅ c. By using differential scanning calorimetry, the melting and crystallization points were determined to be 550 and 510 °C, respectively. Luminescence and scintillation properties were systematically studied. Upon ultraviolet light (360 nm) excitation, the Cs 4 YbI 6 crystal exhibits bluish-green emission centered at 450 and 480 nm due to spin-allowed and spin-forbidden transitions of Yb 2+ activators. The lifetimes of the corresponding emission bands at room temperature are tens and hundreds of nanoseconds, respectively. X-ray excited radioluminescence spectrum is dominated by the spin-forbidden transition of Yb 2+ at 480 nm. The absolute light yield is 2700 ± 200 photons/MeV with a principal scintillation decay time of 33 ns. The physical explanation for the low light yield observed is proposed from experimental and theoretical insights. [ABSTRACT FROM AUTHOR]

In this paper, we present the photoluminescence and scintillation performance of Pr3+ doped (Lu 0.75 Y 0.25) 3 Al 5 O 12 single crystals as a function of Li+ concentration. Lithium concentration had no effect on the optical properties of LuYAG: Pr single crystal scintillators regardless of concentration. On the other hand, scintillation light yield increased by as much as 94% with the incorporation of lithium as a codopant, and the energy resolution at 662 keV was improved to 4.1%, which is an outstanding energy resolution for an oxide single crystal scintillator. Lithium codoping slightly lengthened the fast component of the scintillation decay time, and slightly decreased the contribution from the slow component. Additionally, the samples were annealed in air and scintillation properties were compared before and after this annealing treatment. The change in scintillation properties is explained through the analysis of thermoluminescence glow curves. • Li codoping of LuYAG: Pr can increase light yield, improve energy resolution. • Air annealing improves light yield of LuYAG: Pr, Li by reducing trap concentration. • Thermoluminescence suggests traps play important role in scintillation mechanism. [ABSTRACT FROM AUTHOR]