In this research article, a leftover of Cymbopogon flexuosus stem (CFS) collected from the oil extraction industry was examined for its ability as a reinforcing agent in a polymer composite. Anatomical, morphological, physical, chemical, mechanical, and thermal characteristics of the CFS fiber were examined. Chemical analysis revealed the presence of higher amount of cellulose (68.13%), which offers better bonding properties and higher tensile strength (431.19 ± 23.96 MPa). Moreover, the density of the fiber (1270 kg/m3) found using physical analysis was less than that of synthetic fibers, which paves a path in replacing hazardous synthetic fiber. Solid-state nuclear magnetic resonance and Fourier transform infrared spectrum spectroscopy analyses were conducted to study the functional groups of the extracted CFS fiber. The thermal stability (253.17°C), activation energy (73.01 kJ/mol), and maximum degradation temperature (345.08°C) were investigated by thermogravimetric analysis. X-ray diffraction analysis confirmed the semi-crystalline nature of the fiber with crystallinity index (46.02%) and crystallite size (13.96 nm). The CFS had a smooth surface, as conformed by an atomic force microscopy and scanning electron microscope analysis. Altogether, this study highlights the feasibility of leftover CFS fiber residue as reinforcement in biopolymer matrices replacing synthetic fiber.

A novel epoxy-based composites were fabricated by reinforcing pineapple/flax (PF) fibers and peanut oil cake (PCF) filler using the hand layup cum compression moulding technique and investigated its mechanical, water absorption and wear properties as a function of wt.% of PF fibers (20–40 wt.%) and PCF (1–3 wt.%). The XRD and FTIR results proved the presence of lignocellulosic nature in PCF. Mechanical test results showed significant enhancement in the properties after the addition of PCF. The maximum tensile, flexural and impact properties of 37. 89 MPa, 70.28 MPa and 96.99 J/m were observed in the composites having 20 wt.% of PF and 2 wt.% of PCF. Taguchi based optimization observed a lower specific wear rate (SWR) with 2 wt.% PCF/20 wt.% PF/5 N load and 1500 m sliding distance (SD) combination. The ANOVA results proved the significance of PCF, PF fiber, sliding distance, and load for SWR in this experimentation. The Taguchi optimized results observed a lower coefficient of friction (COF) in 2 wt.% PCF/20 wt.% PF/5N load/500 m SD combination. SEM results displayed surface deformations in the wear-tested composites.