The aim of this study executed on Silicon Nitride (Si3N4) yarn is to examine some bending damage behaviors and fracture mechanisms that occur during the 3D orthogonal fabric forming process. A three point bending experiment device has been developed in order to simulate the Z-binder yarn bending condition. The effects of weft density, fabric thickness, and yarn tension have been studied. The Weibull analysis of the tensile strength show that the bending damage increases with the increase of weft density, fabric thickness, and yarn tension. The resulting bending damage causes a reduction in yarn strength of between 2.5 and 17.2% depending on the bending parameters of yarn. The growth of the fibrillation area also reflects similar trends with tensile strength loss rate. The fibrillation length produced by the yarns is mostly distributed within the range of 0.3 to 0.9 mm. A comparison of the calculation result to experimental data shows the bending fracture probability of filaments inside yarn are less than that of monofilament. The tensile and bending fracture of Si3N4 filaments exhibit typical brittle fracture characteristics. [ABSTRACT FROM AUTHOR]

The effect of normal load on the frictional and wear behaviour of carbon fiber is investigated by simulating the tow-on-tool friction relevant to the beating-up motion of three-dimensional (3 D) weaving process. The true number of contact filaments over a range of normal loads is calculated by characterizing the cross-section parameters of carbon tow. The real contact area is calculated on the basis of the filaments amount by Hertzian contact model. The friction force values obtained from multiplying the real contact area with shear strength are closely with the measured results. The coefficient of friction increases with the increase of normal loads. When the normal load is 250, 400 and 600 mN, the tensile loss rate of the carbon tow after friction test is 6.3%, 23.2% and 42.4% respectively. The filaments reveal multiple fracture damage patterns which are caused by stretching, shearing and compression during the weaving process. [ABSTRACT FROM AUTHOR]