Search

The aim of this study was to evaluate the color stability and the surface roughness of different composites brushed with toothpastes presenting different levels of abrasivity. Thirty discs of each material were obtained using michohybrid composites (Brilliant NG and Charisma Diamond) and a nanocomposite (Filtek Z350XT). The initial color (CIELab) and surface roughness (confocal laser scanning microscopy) of resin discs were evaluated. Afterwards, 10 specimens per group were brushed with the following dentifrices: Maximum Cavity Protection, Sensodyne Repair & Protect and Colgate Sensitive Pro-Relief. Brushing was performed with an electric toothbrush equipped with soft bristle head, with standard power and weight, for 30 minutes. Every 30 seconds, 1.0 ml of the slurry was injected between the bristles of the brush and the specimen. After abrasive challenge, the samples had their color and roughness reevaluated. Data were submitted to the Kruskal-Wallis test (color change) or the t-test (surface roughness). The level of significance was 5%. Results: Brushing did not significantly change the color of the composites tested in the study herein . On the other hand, the surface roughness of the composites was significantly affected by the abrasive challenge, regardless of the toothpaste used. The surface roughness change was similar for all the composites. The abrasive challenge with the toothpastes Maximum Cavity protection, Sensodyne Repair & Protect and Colgate Sensitive Pro-Relief was not able to significantly change the color of the composite resins. Nevertheless, the abrasive challenges significantly altered the surface roughness of all the evaluated composites. However, the changes in surface roughness were statistically similar in the microhybrid and nanofilled composites. Keywords: Composites Resins. Dentifrices. Color. ResumoO objetivo deste estudo foi avaliar a estabilidade de cor e a rugosidade superficial de diferentes resinas compostas escovadas com dentifrícios de diferentes níveis de abrasividade. Trinta discos de cada material foram obtidos utilizando compósitos micro-híbridos (Brilliant NG e Charisma Diamond) e um nanocompósito (Filtek Z350XT). A cor inicial (CIELab) e a rugosidade superficial (microscopia confocal de varredura a laser) dos discos de resina foram avaliadas. Em seguida, 10 amostras por grupo foram escovadas com os dentifrícios Máxima Proteção Anticáries, Sensodyne Repair & Protect e Colgate Sensitive Pro-Alívio. A escovação foi realizada com uma escova elétrica com cabeça de cerdas macias, com potência e peso padronizados, durante 30 minutos. A cada 30 segundos, 1,0 ml da pasta era injetada entre as cerdas da escova e a amostra. Após o desafio abrasivo, as amostras tiveram sua cor e rugosidade reavaliadas. Os dados foram submetidos ao teste de Kruskal-Wallis (alteração de cor) ou ao teste t (rugosidade da superfície) (α=5%). A escovação não alterou significativamente a cor dos compósitos. Por outro lado, a rugosidade superficial dos compósitos foi significativamente afetada pelo desafio abrasivo, independentemente do dentifrício utilizado. A alteração da rugosidade superficial foi semelhante para todos os compósitos. O desafio abrasivo com a Máxima Proteção Anticáries, o Sensodyne Repair & Protect e o Colgate Sensitive Pro-Alívio não foi capaz de alterar significativamente a cor das resinas. Diferentemente, os desafios abrasivos alteraram significativamente a rugosidade superficial de todos os compósitos avaliados. No entanto, as mudanças na rugosidade foram estatisticamente semelhantes nos compósitos micro-híbridos e nanoparticulado. Palavras-chave: Resinas Compostas. Dentifrícios. Cor.

The maternal Immunoglobulin G (IgG) antibodies transferred during the intrauterine life represents the main newborn immune protection against several intestinal and respiratory infection. However, there is little information about the reactivity and function of IgG from cord blood against newborn oral colonization. The aims this study was to evaluate the presence of IgG against Streptococcus mitis, Streptococcus mutans and theirs mains virulence antigens (GbpB, Ag I/II and Gtf) in peripheral blood (PB) samples from mothers with S. mutans or not in the saliva (SA) and compare with umbilical cord blood (CB). PB and SA samples were obtained from healthy women in the Hospital admission and CB was collected after delivery. The specificity of IgG against the bacterial extracts was determined by Western blot. The genetic material detection of S. mutans in the salivas was realized by the quantitative polymerase chain reaction with specific primers. The results showed that the minority of blood samples showed IgG against S. mitis. On the other hand, the majority of samples exhibited IgG anti S. mutans. The number of reactive bands to S. mutans was significantly higher than against S. mitis in both blood samples (p0.05) in the PB from mothers colonized or not by S. mutans. In opposite, in CB sample, it was more frequent to find samples with IgG anti-S. mutans and GbpB in the salivas from mothers with detectable S. mutans (p 0,05) no SP de mães colonizadas ou não por S. mutans. Por outro lado, nas amostras SC, foi mais frequente encontrar amostras com IgG anti-S.mutans e GbpB em salivas de mães com S. mutans detectáveis (p

The objective of this in vitro study was to evaluate the influence of the Er,Cr:YSGG laser associated or not to a desensitizing agent in the treatment of erosive lesions. Forty specimens with dimensions of 4mm x 4mm and 3mm thickness were divided into 4 groups (n = 10): G1- no treatment; G2- 5% fluoride varnish; G3- Er,Cr: YSGG; G4 - fluoride varnish + laser. The specimens were immersed in erosive drink 3 times a day for 1 minute with an average interval of 2 hours between cycles for a period of 10 days. The treatments were performed according to the groups and the surface roughness and the wear profile were analyzed by scanning confocal microscopy. The normality (Kolmogorov-Smirnov) and homogeneity (Levene's) of the tests were evaluated. After these analyzes, the surface roughness data were submitted to the statistical analysis of Variance Analysis (ANOVA). All tests adopted a significance level of 5% (α = 0.05). At the representative images of the wear profile, the morphology of bovine dental enamel in its control and eroded areas were compared and qualitatively discussed. As regard surface roughness, there was no statistically significant difference between the groups. The qualitative analysis of the loss of volume showed that all experimental groups showed significant superficial morphology differences. Considering the limitations of an in vitro study, it can be concluded that the treatments performed were not able to treat dental erosion satisfactorily, indicating the need for more treatment sessions. Keywords: Tooth Erosion. Dental Enamel. Fluoride. YSGG Laser. ResumoO objetivo desse estudo in vitro foi avaliar a influência do laser Er,Cr:YSGG associado ou não a um agente dessensibilizante no tratamento de lesões erosivas. Foram confeccionados 40 espécimes com dimensões de 4mm x 4mm e 3mm de espessura, divididos em 4 grupos (n=10): G1- nenhum tratamento; G2- verniz fluoretado 5%; G3- aplicação do laser Er,Cr:YSGG; G4- verniz fluoretado + laser. Os espécimes foram imersos em bebida erosiva, 3 vezes por dia, durante 1 minuto, com intervalo médio de 2 horas entre os ciclos, por um período de 10 dias. Os tratamentos foram realizados de acordo com os grupos e que foram analisados a rugosidade superficial e o perfil de desgaste por meio de microscopia confocal de varredura. Avaliou-se a normalidade (Kolmogorov-Smirnov) e homogeneidade (Levene’s) dos dados. Após estas análises, os dados de rugosidade superficial foram submetidos ao teste estatístico de Análise de Variância (ANOVA). Todos os testes adotaram nível de significância de 5% (α=0,05). Através da obtenção das imagens representativas do perfil desgaste, a morfologia do esmalte dental bovino em suas áreas controle e erodida foram comparadas e qualitativamente discutidas. Quanto à rugosidade superficial, não houve diferença estatisticamente significativa entre os grupos. A análise qualitativa da perda de volume mostrou que todos os grupos experimentais apresentaram diferenças significativas na morfologia superficial. Considerando as limitações de um estudo in vitro pode-se concluir que os tratamentos realizados não foram capazes de tratar a erosão dentária de forma satisfatória, indicando a necessidade de mais sessões de tratamento. Palavras-chave: Erosão dentária. Esmalte dental. Flúor. Laser de YSGG.

Early diagnosis of white spot lesions allows non-invasive treatment to be indicated for the remineralization of active lesions. The goal was to report the clinical Protocol for the treatment of white spot lesion of a patient by the technique of resin infiltration, observing whether there is change of color on the white spot of the dental enamel after its treatment. The selected patient was 16 years old with good overall health, who featured white spot lesion of the dental enamel on tooth 13, classified as ICDAS score 2. The tooth was photographed, and its color was evaluated with the spectrophotometer in accordance with the CIELhC system. For comparison purposes, the color of tooth enamel in an area adjacent to the lesion was evaluated. The treatment of the lesion was performed with the resin infiltrate Icon (DMG, Hamburg, Germany), following the manufacturer's instructions. The color of the tooth was re-evaluated after the application of the resin infiltrate. At the end of the procedure, it was observed that the treatment of white spot lesion by resin infiltration technique reached its goal because, in addition to being minimally invasive, it was highly approved by patient and it provided the masking of the white spot lesion on the dental enamel. Keywords: Dental Caries. Dental Enamel. Composite Resins. ResumoO diagnóstico precoce de lesões de mancha branca permite que um tratamento não invasivo seja indicado para a remineralização das lesões ativas. O objetivo foi relatar o protocolo clínico para tratamento de lesão de mancha branca ativa de um paciente pela técnica do infiltrante resinoso, observando se existe alteração de cor da mancha branca do esmalte dental após o seu tratamento. Foi selecionada uma paciente, de 16 anos de idade, com boa saúde geral e que apresentava lesão de mancha branca no esmalte dental do dente 13, classificada pelo escore 2 do ICDAS. O dente foi fotografado e sua cor foi avaliada com o espectrofotômetro de acordo com o sistema CIELhC. Para fins de comparação, foi avaliada a cor do esmalte dental em uma área adjacente à lesão. O tratamento da lesão foi realizado com a resina infiltrante Icon (DMG, Hamburgo, Alemanha), seguindo as recomendações do fabricante. A cor do dente foi reavaliada após a aplicação do infiltrante. Ao final do procedimento, observou-se que o tratamento da lesão de mancha branca pela técnica da resina infiltrante atingiu seu objetivo pois, além de ter sido minimamente invasiva, foi bem avaliada pela paciente e proporcionou o mascaramento da lesão de mancha branca do esmalte dental. Palavras-chave: Cárie Dentária. Esmalte Dentário. Resinas Compostas.

O objetivo deste trabalho in vitro foi avaliar a influência de diferentes agentes remineralizantes no tratamento de lesões erosivas em esmalte. Foram confeccionados espécimes de 4mmx4mm e 3 mm de espessura a partir da superfície vestibular de incisivos bovinos (n=10) e divididos aleatoriamente em 4 grupos. G1=aplicação do dentifrício remineralizante, G2= aplicação do agente potencializador remineralizante, G3= dentifrício remineralizante + agente potencializador remineralizante, G4=aplicação de verniz fluoretado (controle positivo), G5=nenhum tratamento (controle negativo). Os espécimes foram imersos em refrigerante durante um período de 10 dias. A rugosidade superficial foi analisada por meio de microscopia confocal de varredura a laser. Os dados foram analisados quanto à homogeneidade (Levene’s) e normalidade (Kolmogorov- Smirnov). Foram realizados testes paramétricos com análise de variância a dois critérios: fator tempo e fator tratamento, e pós-teste de Tukey para diferenciação das médias. Todos os testes estatísticos tiveram nível de significância de 5% (α=0,05). Os resultados obtidos mostraram diferenças estatisticamente significantes, demonstrando a redução da rugosidade da superfície do esmalte logo após o primeiro tratamento (G3) e para os demais grupos (G1, G2 e G4) somente após o segundo tratamento. Concluiu-se que a utilização de dentifrício composto por silicato de cálcio e fosfato de sódio influenciou na rugosidade do esmalte erodido do dente bovino.Palavras-chave: Dentifrícios. Erosão Dentária. Esmalte Dentário.Abstract The objective of this in vitro study was to evaluate the influence of different remineralizing agents in the treatment of enamel erosive lesions. Specimens of 4mmx4mm and 3mm thickness were made from the buccal surface of bovine incisors (n=10) and randomly divided into 4 groups. G1 = application of the remineralizing dentifrice, G2 = application of the remineralizing agent, G3 = remineralizing dentifrice + remineralizing agente, G4 = application of fluoride varnish (positive control), G5 = no treatment Specimens were immersed in refrigerant solution during a period of 10 days. The surface roughness was analyzed by means of confocal laser scanning microscopy. The data were analyzed for homogeneity (Levene's) and normality (Kolmogorov-Smirnov). Parametric tests with analysis of variance were performed on two criteria: time factor and treatment factor, and Tukey post-test for differentiation of means. All tests were statistically significant at 5% (α = 0.05). The results showed statistically significant difference, demonstrating the reduction of surface roughness after the first treatment (G3) and the other groups (G1, G2 and G4) only after the second treatment. It was concluded that the use of dentifrice composed of calcium silicate and sodium phosphate influenced the roughness of the eroded tooth enamel of the bovine tooth.Keywords: Dentifrices. Tooth Erosion. Tooth Enamel.

Resumo A resina composta e o material restaurador mais utilizado atualmente. Apesar de seu sucesso clinico, o material esta sujeito a alteracoes em suas propriedades fisicas, quando exposto ao meio bucal. O objetivo foi avaliar a influencia da degradacao quimica na estabilidade de cor e na rugosidade superficial de resinas micro-hibrida e nanoparticulada. Foram confeccionados 40 discos (6,0mm x 2,0mm) da resina composta micro-hibrida (Z250XT) e 40 da resina nanoparticulada (Z350XT). Apos a analise da cor inicial e da rugosidade inicial, 10 discos de cada resina foram imersos em saliva artificial (Controle, pH=6,4), suco de laranja (pH= 3,4), refrigerante de limao (pH=2,9) e vinho tinto (pH=3,1), por 4 horas por dia (37oC) durante 30 dias. Apos, foram realizadas as leituras finais de cor e rugosidade. Os dados obtidos para a estabilidade de cor foram analisados pelo Teste de Kruskal-Wallis, seguido pelo Teste de Dunn (α=5%). Para a analise da rugosidade foi utilizado o Teste t para amostras pareadas (α=5%). O manchamento provocado pela saliva artificial, suco de laranja e refrigerante foi similar, mas foi estatisticamente diferente do manchamento produzido pelo vinho, em ambas as resinas testadas. O vinho produziu o mesmo grau de manchamento nas resinas micro-hibrida e nanoparticulada. Foi observado que o suco de laranja, o refrigerante e o vinho promoveram aumento da rugosidade superficial dos discos de resina. Diante disso, concluiu-se que o vinho alterou a cor de resinas compostas micro-hibrida e nanoparticulada, e que a rugosidade superficial dos discos de resina foi alterada por todas as bebidas utilizadas. Palavras chave : Resinas Compostas. Corantes. Cor. Abstract Composite resin is the most used restorative material. Despite its clinical success, it is susceptible to changes in its physical properties when exposed to the oral environment. The aim was to evaluate the influence of acidic beverages on the color stability and on the surface roughness of the nanofilled and micro hybrid composite. Forty discs (6.0mm x 2.0mm) of the micro hybrid composite (Z250XT) and 40 of the nanofilled composite (Z350XT) were manufactured. After the measurement of the initial color and the initial roughness, 10 discs of each composite were individually immersed in artificial saliva (control, pH = 6.4), orange juice (pH=3.4), lime soda (pH = 2.9) and red wine (pH = 3.1) during 4 hours per day at 37°C for 30 days. At the end of the experiment, the final analysis of color and surface roughness were performed. The data obtained for the color stability were analyzed by Kruskal-Wallis and Dunn’s test (α= 5%). For the analysis of the surface roughness, the t test for related samples was used (α= 5%). The color changes promoted by artificial saliva, orange juice and soda were similar, but they were statistically different from staining produced by wine, in both tested composites. Wine produced the same degree of staining in both composites. Orange juice, soda and red wine increased the surface roughness of the composite discs. It was concluded that red wine significantly changes the color of micro hybrid and nanofilled composites. Furthermore, all beverages increased the surface roughness of the composites tested in the study herein. Keywords : Composite Resins. Coloring Agents. Color.

A hipersensibilidade dentinária (HD) é caracterizada por uma dor aguda, de curta duração, causada pela movimentação de fluidos no interior de túbulos dentinários expostos ao meio bucal. Recentemente, a utilização dos lasers de alta e baixa intensidade foi proposta como uma alternativa para o tratamento da HD. Este trabalho realizou uma revisão da literatura baseada em artigos publicados entre 2009 e 2013 sobre os efeitos dos lasers baixa e alta intensidade para o tratamento da HD. A base de dados utilizada foi o PubMed utilizando-se as palavras-chave Dentin hypersensitivity, laser, Nd:YAG, Er:YAG, GaAlAs, Er,Cr:YSGG, CO2, HeNe, hydrodinamic theory. Foi observado que o tratamento da HD com lasers é um método biocompatível, não-invasivo e eficiente. Os lasers de baixa intensidade (HeNe e GaAlAs) estimulam as células nervosas do tecido pulpar, interferindo na polaridade das membranas celulares pelo aumento da amplitude do potencial de ação, levando ao bloqueio da transmissão do estímulo ao sistema nervoso central, e estimulam os odontoblastos a produzirem dentina reparadora, o que diminui a permeabilidade da dentina e interrompe a movimentação de fluidos nos túbulos dentinários. Os lasers em alta intensidade (Nd:YAG, Er:YAG, Er,Cr:YSGG e CO2) têm o objetivo de obliterar a embocadura dos túbulos dentinários através da irradiação direta da dentina exposta ao meio bucal, promovendo a dissolução e a ressolidificação dos cristais de hidroxiapatita da dentina, levando à eliminação da sensibilidade dolorosa por um tempo prolongado. Pode-se concluir que os lasers de alta e baixa intensidade são efetivos para o tratamento da hipersensibilidade dentinária cervical.