Search

Nanoparticles of MgO, Al(2)O(3), CaO and SiO(2) were synthesized using aerogel route, and characterized by N(2)-BET, SEM, TEM, XRD, TGA and FT-IR techniques. Characterization indicated 2-75 nm diameter nanoparticles with 135-887 m(2)/g surface area and microporous-mesoporous characteristics. Prepared nanoparticles were tested for their adsorptive potential by conducting studies on kinetics of adsorption of diethylchlorophosphate under static conditions. The kinetic parameters such as equilibration constant, equilibration capacity, diffusional exponent and adsorbate-adsorbent interaction constant have been determined using linear driving force model and Fickian diffusion model. AP-MgO and AP-CaO showed the maximum (1011 mg/g) and minimum (690 mg/g) uptake of DEClP, respectively. All nanoparticles showed the values of diffusional exponent to be >0.5, indicating the diffusion mechanism to be anomalous. Hydrolysis reaction (identified using GC/MS technique) was found to be the route of degradation of DEClP., (Copyright 2010 Elsevier B.V. All rights reserved.)

Nanoparticles of AP-Al(2)O(3) (aero-gel produced alumina) have been produced by an alkoxide based synthesis involving aluminum powder, methanol, toluene and water. Thus produced alumina nanoparticles were characterized and the data indicated the formation of nanoparticles of alumina in the size range of 2-30 nm with high surface area (375 m(2)/g). Thereafter, these nanoparticles were impregnated with reactive chemicals. Adsorptive removal kinetics for DEClP (diethylchlorophosphate) and GB (isopropylmethylphosphonofluoridate, sarin) was monitored by GC-FID (gas chromatograph coupled with flame ionization detector) technique and found to be following pseudo first order reaction kinetics. Among impregnated AP-Al(2)O(3) nanoparticles based sorbent systems AP-Al(2)O(3) impregnated with 9-molybdo-3-vanadophosphoric acid (10%, w/w) was found to be the most reactive with least half-life values of 7 and 30 min for the removal of DEClP and GB, respectively, whereas unimpregnated AP-Al(2)O(3) nanoparticles showed the best adsorption potential among all studied systems. In addition to this, hydrolysis reaction {identified using GC/MS (gas chromatograph coupled with mass spectrometer) technique} was found to be the route of degradation of DEClP and GB on impregnated alumina nanoparticles., ((c) 2009 Elsevier B.V. All rights reserved.)

Active carbon, grade 80 CTC, of surface area 1199m(2)/g, 12x30 BSS particle size and coconut shell origin was impregnated (5%, W/W) with various impregnants such as Cu(II) 1,1,1,5,5,5-hexafluoroacetylacetonate, Cu(II) 1,1,1-trifluoroacetylacetonate, 1-phenylbute-1,3-dione-2-oxime plus Cu(II) using incipient wetness technique. These impregnated carbons along with active carbon (Grade 80 CTC) and whetlerite were studied for the adsorption of dimethyl methylphosphonate (DMMP) at 33+/-1 degrees C under static conditions. Cu(II) 1,1,1,5,5,5-hexafluoroacetylacetonate impregnated carbon system showed highest uptake (68.5%, W/W) of DMMP amongst all the carbon systems, however, active carbon with higher surface area could adsorb 61.5% (W/W) of DMMP under same conditions. It indicated that the adsorption by Cu(II) 1,1,1,5,5,5-hexafluoroacetylacetonate impregnated carbon was not only due to physisorption but chemisorption as well. Kinetics of adsorption was also studied and various parameters such as equilibration time, equilibration capacity, rate constant (k), diffusional exponent (n) and constant (K) were determined. Carbons with and without DMMP exposure were also studied using IR and TGA techniques. Reaction products were analyzed using gas chromatography coupled with mass spectrometry (GC/MS) and found to be methyl methylphosphonic acid (MMPA) and methylphosphonic acid (MPA) for Cu(II) 1,1,1,5,5,5-hexafluoroacetylacetonate impregnated carbon.

Abstract: Nanoparticles of AP-Al2O3 (aero-gel produced alumina) have been produced by an alkoxide based synthesis involving aluminum powder, methanol, toluene and water. Thus produced alumina nanoparticles were characterized and the data indicated the formation of nanoparticles of alumina in the size range of 2–30nm with high surface area (375m2/g). Thereafter, these nanoparticles were impregnated with reactive chemicals. Adsorptive removal kinetics for DEClP (diethylchlorophosphate) and GB (isopropylmethylphosphonofluoridate, sarin) was monitored by GC–FID (gas chromatograph coupled with flame ionization detector) technique and found to be following pseudo first order reaction kinetics. Among impregnated AP-Al2O3 nanoparticles based sorbent systems AP-Al2O3 impregnated with 9-molybdo-3-vanadophosphoric acid (10%, w/w) was found to be the most reactive with least half-life values of 7 and 30min for the removal of DEClP and GB, respectively, whereas unimpregnated AP-Al2O3 nanoparticles showed the best adsorption potential among all studied systems. In addition to this, hydrolysis reaction {identified using GC/MS (gas chromatograph coupled with mass spectrometer) technique} was found to be the route of degradation of DEClP and GB on impregnated alumina nanoparticles. [Copyright &y& Elsevier]