The objective of this study was to investigate how the connection of superstructures to implants with different surface properties affects the surrounding bone. The right and left mandibular premolars and molars of 5 dogs were extracted. After 12 weeks, a machined implant was placed mesially and an anodized implant was placed distally on one side of the edentulous jaw, with the positions reversed on the opposite side. Twelve weeks after implantation, splinted superstructures were set to the implants. At 24 weeks after implantation, the implant stability quotient (ISQ) was measured, radiographs were obtained. Removal torque values were measured and histologic observation was performed. The ISQ values at 24 weeks after implantation were not significantly different between the groups. The removal torque values were significantly different between the distal anodized and distal machined implants (p &lt, 0.05). From 12 to 24 weeks, marginal bone losses were not significantly different between the groups. Fluorescent observation of tissue samples revealed bone-remodeling activity around all of the implants. The results of this study suggest that when implants with different surface properties are connected, machined implants at the most distal sites might be a potential risk factor for implant-bone binding.

Evaluating primary stability is important to predict the prognosis of dental implant treatment. Primary stability is decreased in a low bone density site such as osteoporosis. However, it is difficult to apply in small animal and the effect of the different implant surface topography for the primary stability at low bone density site has not yet fully been investigated. The purpose of the present study was to evaluate the influence of implant surface topography on primary stability in a standardized osteoporosis animal model. Six rabbits underwent ovariectomy and administrated glucocorticoid to induce an osteoporosis model. Sham-operations were performed in additional six rabbits. Implants with machined or oxidized-surfaces were inserted into the femur epiphyses and insertion torque (IT) and implant stability quotient (ISQ) were measured. In sham model, the IT and ISQ did not differ significantly between the both implant. However, the IT value of oxidized-surface implant was significantly higher than that of the machined implant in the osteoporosis model. Meanwhile, ISQ did not significantly differ between the machined and oxidized-surfaced implants. In conclusion, the IT of implants is higher with rough than with smooth surfaces but that there are no differences in ISQ value between different surfaces in a standardized osteoporosis bone reduced rabbit model.