Search

Nitrogen enriched carbon adsorbents with high surface areas were successfully prepared by carbonizing the low-cost urea formaldehyde resin, followed by KOH activation. Different characterization techniques were used to determine the structure and surface functional groups. Maximum surface area and total pore volume of 4547 m 2  g -1 and 4.50 cm 3  g -1 were found by controlling activation conditions. The optimized sample denoted as UFA-3-973 possesses a remarkable surface area, which is found to be one of the best surface areas achieved so far. Nitrogen content of this sample was found to be 22.32%. Dynamic CO 2 uptake capacity of the carbon adsorbents were determined thermogravimetrically at different CO 2 concentrations (6-100%) and adsorption temperatures (303-373 K) which have a much more relevance for the flue gas application. Highest adsorption capacity of 2.43 mmol g -1 for this sample was obtained at 303 K under pure CO 2 flow. Complete regenerability of the adsorbent over four adsorption-desorption cycles was obtained. Fractional order kinetic model provided best description of adsorption over all adsorption temperatures and CO 2 concentrations. Heterogeneity of the adsorbent surface was confirmed from the Langmuir and Freundlich isotherms fits and isosteric heat of adsorption values. Exothermic, spontaneous and feasible nature of adsorption process was confirmed from thermodynamic parameter values. The combination of high surface area and large pore volume makes the adsorbent a new promising carbon material for CO 2 capture from power plant flue gas and for other relevant applications., (Copyright © 2018 Elsevier Ltd. All rights reserved.)

In this work, we report carbon adsorbents obtained from high nitrogen content melamine-formaldehyde resin as starting material and mesoporous zeolite MCM-41 as template through nanocasting technique. To synthesize different carbon structure adsorbents with improved textural and surface properties, the material undergo carbonization followed by physical activation under CO 2 atmosphere at different temperatures. Characterizations of the adsorbents using SEM, TEM, XPS, nitrogen sorption, CHN, TKN, and TPD have been carried out. Characterization results reveal the development of nanostructured carbon adsorbents with better texture and surface properties as compared to the sample prepared by direct carbonization. Sample prepared at carbonization-activation temperature of 700 °C shows highest basicity, surface area (193.28 m 2  g -1 ) and pore volume (0.32 cm 3  g -1 ). Performance evaluation of adsorbent was performed thermo gravimetrically at different temperatures and concentrations and was found that the adsorbent synthesized at 700 °C exhibit highest CO 2 uptake of 0.93 mmol g -1 with nitrogen content of 22.73%. It was found that both surface area and nitrogen functional group have a major impact on adsorption capacity. Physiosorption process was confirmed by a decrease in adsorption capacity with increase in temperature. Three kinetic models and isotherms were used in this study and found that fractional order kinetic model and Freundlich isotherm best fitted with the experimental data. Isotherm study depicts the heterogeneous nature of adsorbent surface. Adsorbent exhibited complete regenerability and was stable over four adsorption-desorption cycles. Low value of isosteric heat of adsorption of 15.75 kJ mol -1 , indicates physiosorption process. Negative value of ΔG 0 and ΔH 0 confirms spontaneous, feasible and exothermic nature of adsorption process., (Copyright © 2017 Elsevier Ltd. All rights reserved.)

Nanostructured carbon adsorbents containing high nitrogen content were developed by templating melamine-formaldehyde resin in the pores of mesoporous silica by nanocasting technique. A series of adsorbents were prepared by altering the carbonization temperature from 400 to 700 °C and characterized in terms of their textural and morphological properties. CO2 adsorption performance was investigated at various temperatures from 30 to 100 °C by using a thermogravimetric analyzer under varying CO2 concentrations. Multiple adsorption-desorption experiments were also carried out to investigate the adsorbent regenerability. X-ray diffraction (XRD) and transmission electron microscopy (TEM) confirmed the development of nanostructured materials. Fourier transform infrared spectroscopy (FTIR) and elemental analysis indicated the development of carbon adsorbents having high nitrogen content. The surface area and pore volume of the adsorbent carbonized at 700 °C were found to be 266 m(2) g(-1) and 0.25 cm(3) g(-1) respectively. CO2 uptake profile for the developed adsorbents showed that the maximum CO2 adsorption occurred within ca. 100 s. CO2 uptake of 0.792 mmol g(-1) at 30 °C was exhibited by carbon obtained at 700 °C with complete regenerability in three adsorption-desorption cycles. Furthermore, kinetics of CO2 adsorption on the developed adsorbents was studied by fitting the experimental data of CO2 uptake to three kinetic models with best fit being obtained by fractional order kinetic model with error% within range of 5%. Adsorbent surface was found to be energetically heterogeneous as suggested by Temkin isotherm model. Also the isosteric heat of adsorption for CO2 was observed to increase from ca. 30-44 kJ mol(-1) with increase in surface coverage., (Copyright © 2015 Elsevier Ltd. All rights reserved.)