Search

Introduction This study aimed to investigate dental pulp responses to novel bioactive glass (BG) pulp capping materials after direct pulp capping in vivo . Methods Novel BG pulp capping materials are composed of powder and fluid. The powder is BG (82.36% SiO 2 , 15.36% CaO, and 2.28% P 2 O 5 ), and the fluid is provided in 2 kinds: (1) phosphate buffer solution (BG-PB) and (2) phosphate buffer solution with the addition of 1 wt% sodium alginate (BG-PB-SA). After mixing the powder and fluid, BG-PB and BG-PB-SA were prepared. Cavities with mechanical pulp exposure were prepared on maxillary first molars of Wistar rats. The exposures were randomly capped with BG-PB, BG-PB-SA, or mineral trioxide aggregate (MTA). After 1 ( n = 6) and 4 weeks ( n = 8), maxillary segments were obtained and prepared for histologic analysis with a scoring system. Statistical analysis was performed using the Kruskal-Wallis and Mann-Whitney U tests with the significance set at .05. Results After 1 week, few inflammatory cells were present in the BG-PB, BG-PB-SA, and MTA groups. Moreover, a thin layer of newly generated matrix was observed in most specimens. After 4 weeks, all specimens from the 3 groups formed a heavy dentin bridge. BG-PB and BG-PB-SA groups exhibited no or slight inflammatory response, whereas the MTA group exhibited a slight to moderate inflammatory response. No significant difference was observed in pulp inflammation and dentin formation among the 3 groups at either time point ( P > .05). Conclusions When used as a pulp capping agent, BG-PB and BG-PB-SA had similar favorable cellular and inflammatory pulp responses to those of MTA. Therefore, BG is a promising pulp capping material.

The purpose of this study was to compare Biodentine and mineral trioxide aggregate (MTA) for direct pulp capping in young permanent molars by clinical and radiographic evaluation in 7- to 9-year-old children.In 50 patients, 29 patients with bilateral asymptomatic first permanent molars with carious involvement were selected. According to split mouth design, these patients were then divided into 2 groups, Biodentine group (right side) and MTA group (left side). The pulp-capping procedure was performed by using Biodentine and MTA in 58 asymptomatic bilateral permanent molars with pulp exposure. At each recall (baseline, 6 and 12 months), treatment outcome was assessed clinically through pulpal sensitivity tests as well as radiographically to evaluate dentin bridge formation.The study reported 100% success rate with both Biodentine and MTA at baseline and 6- and 12-month follow-up on the basis of clinical and radiographic parameters. These findings were statistically non-significant (P .05) between both groups (Biodentine and MTA). Radiographically, dentin bridge formation was not evident with both groups at baseline, but it was evident after 6- and 12-month follow-up. These findings were statistically non-significant (P .05) in both Biodentine and MTA groups.This study reported 100% success rate with both MTA and Biodentine when used as direct pulp-capping agent in first permanent molars in 7- to 9-year-old children. The major limitations of the study were smaller sample size and short follow-up period.

Introduction: A number of vital pulp therapy techniques havebeenrecommended to preserve pulpvitality in teeth with complicated crown fractures, especially in young patients. Calcium hydroxide has been the gold standard as a pulp capping material, but recently mineral trioxide aggregate (MTA) has been recommended. This case report describes the treatment of tooth discoloration caused by white MTA (WMTA) used for the management of a complicated crown fracture. Methods: A partial pulpotomy was performed with the use of WMTA after a complicated crown fracture of the upper right central incisor. Seventeen months later, the WMTA was removed because of tooth discoloration, and internal bleaching was performed. Results: Upon access, the WMTA was completely discolored. After it was removed, a significant color change was observed in the tooth crown, which was further improved with internal bleaching. The tooth remained vital, and a dentin bridge was confirmed clinically and radiographically. Conclusions: The recommendation to use WMTA for vital pulp therapy in the esthetic zone may need to be reconsidered. Should discoloration occur with the use of WMTA, the technique described may be used to improve the esthetics. (J Endod 2011;37:1017‐1020)

The aim of this study was to investigate the response of human pulp tissue to a dentin bonding agent, Scotchbond Multi-Purpose Plus (SMPP), in exposed class V cavities. Sixteen human premolar teeth were mechanically exposed. Ten pulps were capped with SMPP and six teeth were capped with Dycal. The cavities were filled with a composite. After 40 days, the teeth were extracted and processed for histologic evaluation. Of the 10 teeth capped with SMPP, eight showed moderate chronic inflammation, one was severely inflamed, and one pulp had no to slight inflammation. None of the teeth capped with SMPP showed dentin bridge formation. Of the six teeth capped with Dycal, three exhibited incomplete dentin bridges associated with no to slight inflammation, and three showed no to slight inflammation, without formation of dentin bridges. Direct capping with Dycal with subsequent sealing with SMPP may show favorable results in pulp tissue. SMPP may cause inflammatory changes when applied directly to exposed pulp tissue.

Mineral trioxide aggregate (MTA) is a biocompatible material for direct pulp capping. This study was designed to compare the clinical outcomes of pulp-exposed teeth treated with either poly(ε-caprolactone) fiber mesh (PCL-FM) as a barrier for MTA (so-called PCL-FM/MTA) or MTA direct pulp capping.Sixty human vital teeth were evenly divided into 4 groups (n = 15 in each group). Teeth in groups 1 and 3 had pulp exposure1 mm in diameter, whereas teeth in groups 2 and 4 had pulp exposure of 1-1.5 mm in diameter. Teeth in groups 1 and 2 were treated with PCL-FM/MTA direct pulp capping, and those in groups 3 and 4 were treated with MTA direct pulp capping.Teeth treated with PCL-FM/MTA direct pulp capping needed a significantly shorter mean duration for dentin bridge formation than teeth treated with MTA direct pulp capping. Moreover, teeth with pulp exposure1.0 mm in diameter needed a significantly shorter mean duration for dentin bridge formation than teeth with pulp exposure of 1-1.5 mm in diameter after either PCL-FM/MTA or MTA direct pulp capping treatment. In addition, teeth treated with PCL-FM/MTA direct pulp capping formed an approximately 3-fold thicker dentin bridge than teeth treated with MTA direct pulp capping 8 weeks or 3 months later. Furthermore, none of the teeth treated with PCL-FM/MTA direct pulp capping showed tooth discoloration after treatment for 3 months.PCL-FM/MTA is a better combination material than MTA alone for direct pulp capping of human permanent teeth.

A quantitative assessment of dentin bridges was conducted on sections prepared from teeth capped with four pulp-capping agents (Bioglass, Life, Demineralized Dentin Matrix, and Teflon) in a micro-swine model. The degree of mineralization of the dentin bridges relative to the adjacent primary dentin was measured using a computer-based image analysis of microradiographs prepared from the sections. The rate of formation of the dentin bridge was measured from fluorescent bands formed in the same sections by a Demeclocycline dentin marker. There were no statistically significant differences in the relative mineral densities of the dentin bridges and the rate of dentin bridge formation under the four pulp-capping agents. These findings support the suggestion that components of the extracellular matrix rather than pulp-capping agents may be important in the formation and mineralization of dentin bridges in repairing dental pulps.

Two case reports with dens evaginatus are presented. Each patient had one tooth affected. There was a prominent tubercle on the occlusal surface of the mandibular second premolar. Under local anesthesia and rubber dam isolation a partial pulpotomy was conducted and mineral trioxide aggregate was placed. After 6 months the teeth were removed as part of planned orthodontic treatment. Histological examination of these teeth showed an apparent continuous dentin bridge formation in both teeth, and the pulps were free of inflammation. These cases show that mineral trioxide aggregate can be used as an alternative to existing materials in the proplylactic treatment of dens evaginatus.

This study was designed to examine the relation between pulpal nerves and the differentiation of pulpal cells into preodontoblasts and odontoblasts during the healing process after pulpotomy. A total of 36 upper and lower teeth obtained from six adult dogs were used. The pulp chamber was opened with a sterile diamond bur, the coronal pulp was exposed, and the whole surface of the amputated pulp was capped with calcium hydroxide. The interval between pulpotomy and extraction was 5, 7, 10, 15, 20, 30, 40, 50, and 60 days, and then specimens were examined ultrastructurally. Close contact between fibroblast-like cells/osteoblast-like cells and nerve terminals at the calcification front was observed in the early healing process after pulpotomy, suggesting a close relation between nerve fibers and pulpal cell differentiation.

The maxillary molars of rats were exposed and treated for five minutes with either Formocresol, formaldehyde, cresol, or glycerol—a control solution-and then covered with zinc oxide-eugenol and amalgam. After the treatment, the animals were killed at weekly intervals for four weeks. Analysis of histolgic sections showed that formaldehyde did not inhibit or enhance pulpal recovery when compared with the control solution. Cresol greatly hindered healing, as indicated by the lack of dentin bridge formation within the time span of this experiment. Formocresol treatment slowed, but did not prevent, the resolution of the defensive reaction.

Wet collagen sponge and wet collagen fabric are better tolerated as pulp capping materials than dry collagen sponge or dry collagen fabric. Dentin bridge formation seems to occur only when an area of surface necrosis subsequently undergoes dystrophic calcification.