The rise of flexible and wearable electronics has spurred advancements in printed, flexible micro-supercapacitors for energy storage. This study presents the fabrication of flexible micro-supercapacitors using a novel nanocomposite of tin dioxide grown on layered reduced graphene oxide through one-pot in situ synthesis. The conductive functional ink, formulated by mixing the nanocomposite, is effectively utilized in screen-printing technology. The resulting micro-supercapacitors, particularly the SG-1 variant, demonstrate impressive electrochemical performance. The nanocomposites show exceptional versatility across various electrolytes, including alkaline, acidic, and quasi-gel electrolytes with a polyvinyl alcohol matrix infused with potassium hydroxide. An in-depth comparison of their efficacy in these electrolytes highlights the most suitable configurations for optimal performance. At a scan rate of 5 mV s−1, SG-1 achieves areal capacitances of 148.7 mF cm−2 and 87.7 mF cm−2 in the 1 M KOH and polyvinyl alcohol infused with 1 M KOH quasi-gel electrolyte. Additionally, SG-1 in the gel electrolyte demonstrates remarkable energy density of 11.7 mWh cm−2 at power density of 490 mW cm−2. Notably, the fabricated micro-supercapacitors exhibit excellent capacitive retention of 89.5% even after undergoing 5000 cycles of charge–discharge, underscoring their robustness and long-term stability for practical applications in flexible and wearable electronics. [ABSTRACT FROM AUTHOR]

The resistive type of graphite/WO3 nanocomposite-based humidity sensor is fabricated through screen printing on a flexible polyethylene terephthalate substrate. Three different nanocomposite-based humidity sensors have been fabricated and analyzed for their humidity-sensing characteristics. The structure elucidation of the nanocomposite was carried out using x-ray diffraction, Fourier-transform infrared spectroscopy, and scanning electron microscopy. By exposing the printed humidity sensor to relative humidity ranging from 11% to 97% at room temperature, its capabilities were studied. The relative resistance, sensitivity, dynamic response, and hysteresis were determined for all three devices, and they showed maximum responses towards relative humidity changes with the highest sensitivity of ≈ 60.8% and excellent hysteresis curves (maximum change of ≈ 1%). The screen-printed flexible humidity sensor exhibited less than a 5% change in the internal electrical resistance when subjected to various bending angles. [ABSTRACT FROM AUTHOR]