Abstract: In this paper, the electrochemical reduction of oxygen has been studied on gold nanoparticle/multi-walled carbon nanotube (AuNP/MWCNT) modified glassy carbon (GC) electrodes in 0.5M H2SO4 using the rotating disk electrode (RDE) method. The AuNP/MWCNT catalysts were prepared by chemical deposition of AuNPs onto MWCNTs spontaneously grafted with 4-nitrophenyl groups. The composite electrode was characterised by transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS) and cyclic voltammetry (CV). The oxygen reduction behaviour of these electrodes was compared with that of a bulk gold electrode. The AuNP/MWCNT catalyst showed a pronounced electrocatalytic activity towards O2 reduction in acid media. The half-wave potential of O2 reduction on the AuNP/MWCNT catalyst shifted ca 80mV to more positive potentials as compared to that of a polished Au electrode. The kinetic parameters of oxygen reduction were determined and the specific activity of the hybrid electrode was slightly higher than that of the bulk Au electrode. [Copyright &y& Elsevier]

In this work the electrocatalysis of oxygen reduction on iron and cobalt phthalocyanine modified reduced graphene oxide/multi-walled carbon nanotube (rGO/MWCNT) composite catalyst has been investigated. Modification of the carbon support was achieved by pyrolysing the mixture of rGO/MWCNT in the presence of metallophthalocyanine compounds at 800 °C. The surface morphology, graphitisation and surface composition of the catalyst materials were characterised by transmission electron microscopy (TEM), scanning electron microscopy (SEM), micro-Raman spectroscopy and X-ray photoelectron spectroscopy (XPS). The oxygen reduction reaction (ORR) was studied in 0.1 M KOH and 0.5 M H 2 SO 4 solutions on glassy carbon electrodes modified with MN 4 -macrocycle/rGO/MWCNT catalysts employing the rotating disk electrode (RDE) method. The RDE results show that both iron and cobalt phthalocyanine modified rGO/MWCNT electrocatalysts are highly active for ORR in alkaline solution while in acid media these materials exhibit only modest ORR activity. [ABSTRACT FROM AUTHOR]