Search

Rubber magnetic composites based on acrylonitrile butadiene rubber and strontium ferrite were cured with standard sulfur-based vulcanization systems as well as an organic peroxide. Zinc methacrylate (ZDMA) as a coagent was applied in both sulfur and peroxide vulcanization of rubber magnets. The aim was to evaluate the influence of ZDMA on curing characteristics and cross-link density of the prepared materials. Subsequently, physical-mechanical and magnetic properties were investigated. The results showed that ZDMA takes an active part in the cross-linking process of composites cured with an organic peroxide. Due to the presence of free radicals formed from peroxide decomposition, molecules of ZDMA polymerize into the nanostructures which can be physically adsorbed or chemically grafted onto rubber chains. Moreover, owing to zinc ions, ZDMA exhibits strong adhesion to ferrite filler and thus it contributes to the improvement of adhesion between the rubber and the filler on the interphase. The overall reinforcement of rubber magnetic composites was subsequently achieved. In the case of rubber magnets cured with the sulfur-based system, ZDMA acts as a conventional filler with a slight reinforcing effect due to the lack of free radicals required for its polymerization. [ABSTRACT FROM AUTHOR]

Barium ferrite in constant amount (50 phr) was incorporated into styrene-butadiene rubber to prepare rubber magnetic composites. Dicumyl peroxide was used as a curing agent for cross-linking of the prepared composites. Four different types of low-molecular-weight organic compounds were applied as coagents to enhance the efficiency of cross-linking process and to improve the compatibility between the rubber and the filler on the interphase. The main goal of this work was to investigate the influence of the composition of peroxide curing system on cross-link density, physical–mechanical and magnetic properties of the composites. The results revealed that the type and amount of coagents have no influence on magnetic properties of the rubber magnets. On the other hand, cross-link density and physical–mechanical properties were significantly dependent on the composition of curing system. The increase of tensile strength can be attributed to the improvement of adhesion on the interphase filler–rubber due to the presence of coagents. [ABSTRACT FROM AUTHOR]

In the first part of the research, rubber magnetic composites were prepared by incorporation of strontium and barium ferrite in concentration scale ranging from 0 to 200 phr into rubber matrices based on acrylonitrile–butadiene rubber and styrene–butadiene rubber. The main objective was to investigate the influence of the type and content of magnetic filler on the cross-link density, physical–mechanical and magnetic characteristics of the prepared composites. In the second part of the study, the content of magnetic fillers was kept on constant level—200 phr and the main aim was to investigate the change in mutual combination of both fillers on the cross-linking and properties of the rubber magnets. The results revealed that both fillers show reinforcement effect in the rubber matrices. The higher tensile strength of composites was achieved by application of barium ferrite. Magnetic properties of composite materials were significantly influenced by magnetic characteristics of magnetic fillers. Higher remanent magnetic induction of barium ferrite was reflected in higher remanent magnetization of the equivalent composites. On the other hand, higher coercivity of strontium ferrite resulted in higher coercivity of strontium ferrite-filled composites. [ABSTRACT FROM AUTHOR]

Rubber magnetic composites were prepared by incorporation of strontium ferrite in concentration scale ranging from 0 phr to 100 phr into rubber matrices based on natural rubber (NR) and acrylonitrile-butadiene rubber (NBR). The composite systems were exposed to the conditions of thermooxidative aging at 70°C for 7, 14, and 28 days. The influence of aging period on the behavior of prepared materials was considered based on investigation of their cross-link density, physical–mechanical, and magnetic characteristics. The results revealed that the influence of thermooxidative aging on composite characteristics is dependent on the type of rubber matrix. The thermooxidative aging was found to have negative effect on the cross-link density and tensile properties of composites based on NR, which were deteriorated in dependence of aging time. The possible influence of magnetic filler content on aging mechanism was observed during last period of aging after which the decrease in cross-link density and tensile characteristics was more pronounced with increasing content of strontium ferrite. By contrast, the cross-link density, modulus, and hardness of composites based on NBR were found to be positively influenced by aging as their values showed increasing trend with extension of aging period. [ABSTRACT FROM AUTHOR]

In the present work, rubber magnetic composites were prepared by incorporation of strontium ferrite into rubber matrices based on natural rubber (NR) and acrylonitrile butadiene rubber (NBR). The sulfur and peroxide curing systems were introduced in cross-linking of rubber matrices. The research was aimed at the evaluation of magnetic filler content and type of curing system on the cross-link density, physical–mechanical and magnetic properties of prepared composites. The relationship between the composition of elastomers and cross-link structure within the rubber matrices, formed by applying different curing systems, was under investigation through strain–stress behavior of tested materials. The achieved results showed that ferrite behaves as a reinforcing filler in peroxide-cured composites based on NR, and in both, sulfur as well as peroxide-cured composites based on NBR. The results also demonstrated that the cross-linking degree and the type of cross-link structure as well as the composition of rubber matrices, to a large extent, influence the property spectrum of tested composite systems. [ABSTRACT FROM AUTHOR]

The goal of the present work was to study the preparation and properties of rubber magnetic composites and investigation of strontium ferrite activity in examined materials. Three types of rubber matrices, namely butadiene rubber as non-polar elastomeric matrix, nitrile butadiene rubber (NBR) and NBR/poly(vinyl chloride) blend as polar elastomeric matrices, were compounded with strontium ferrite and other additives in order to prepare rubber magnetic composites. Ferrite dosage was given in modified and unmodified forms in concentration scale ranging from 0 to 100 phr. The influence of magnetic filler content on the mechanical properties of composites was investigated. Correlation between Wolf activity coefficient and Payne effect in relation to the mechanical properties of tested systems was discussed. The results revealed that the observed characteristics are dependent on the type of rubber matrix and also on the type of ferrite. [ABSTRACT FROM PUBLISHER]