Search

The purpose of this study is to evaluate in detail the usability of new cellulosic fibers extracted from the stem of the plant Strelitzia reginae, as a potential reinforcement for polymer composites. The morphological, physical, thermal, and mechanical properties of fibers were addressed for the first time in this paper. Both untreated and alkali-treated fibers were characterized, using scanning electron microscopy (SEM), Fourier-transform infrared, thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), optical microscope, and X-ray diffraction (XRD) and applying tensile test for determining the mechanical behavior. For both fiber treated at one hour (T1H) and at four hours (T4H), the stem anatomy and fiber SEM micrographs showed a strong presence of fiber cells. Thermogravimetry and DSC showed that the fiber was thermally stable up to 233°C for untreated fiber, 254 and 240°C, respectively, In single-fiber tensile tests, it was observed that the fibers extracted from the stem of Strelitzia reginae were strong. The mean values of Young's modulus exhibited by untreated fibers and treated (T1H) and (T4H) are, respectively, 9.89 GPa, 12.08, and 18.39 GPa. Also mean values of tensile strength are 271.79, 306.23, and 421.39 MPa. The XRD reveals the presence of cellulose with a Crystallinity Index of 70% for raw fiber and 72% for the treated one. Fourier-transform infrared analysis well demonstrated the effect of chemical treatment. It can be concluded from the results of all above experiments that the Strelitzia reginae fibers (SR) could serve as a possible reinforcement in composite materials. [ABSTRACT FROM AUTHOR]

Chicken feathers waste from poultry industry was incorporated in poly(lactic acid) matrix to obtain an environmental friendly biocomposite taking advantage of the unique properties of chicken feathers, such as low density, biodegradability and good thermal and acoustic properties, and of the biodegradability of the poly(lactic acid). The effect of manufacturing conditions on the final properties of the composite and on the matrix–fiber compatibility was studied. Optimal manufacturing conditions, in order to obtain the best mechanical results, were found at a temperature of 170–180℃ for a processing time of 5 min and a speed of mixing of 50 r/min. Young’s modulus was not very affected by the chicken feather’s content showing a maximal variation of less than 8%, indicating that is possible to include chicken feathers in a composite maintaining its stiffness. However, tensile strength and elongation decreased up to 58 and 12%, respectively, when chicken feather content was 25% because of the restraining effect of the fibers. Moreover, dimensional stability was negatively affected with the inclusion of chicken feathers. Infrared spectroscopy and scanning electron microscopy studies show that fiber–matrix interaction exists but it is weak. [ABSTRACT FROM AUTHOR]

The present work describes a biocomposite with thermal and acoustic insulating properties from agricultural or forestry residues using a steam injection molding technique. The biocomposites showed reasonable thermal insulation properties as judged based on their thermal conductivity, thermal diffusivity, and thermal stability data. The biocomposites had also good sound absorption properties. The dimensional stability of the biocomposites under accelerated weathering conditions was almost ideal. Although the flame retardancy of the biocomposites had rating acceptable to building products, it was yet concluded that for the biocomposites to have a wider market share, their flame-retardant capacity should be improved. [ABSTRACT FROM AUTHOR]