Search

Abstract: This paper compares the influence of the molecular weight of polylelectrolytes forming polyelectrolyte multilayers (PEM) on wood fibers on adhesion and paper strength. Sheets were made from fibers treated with poly(allylamine hydrochloride) (PAH)/poly(acrylic acid) (PAA) of molecular mass 70,000 and 240,000, respectively, and of poly(dimethyldiallylammonium chloride) (PDADMAC)/poly(styrene sulfonate) (PSS) of molecular mass 30,000 and 80,000, respectively. The results were compared to what has recently been reported for PEM formation on fibers using a low-molecular-mass combination of PAH and PAA and a high-molecular-mass combination of PDADMAC/PSS. There was a less significant improvement in the case of the low-molecular-mass PDADMAC/PSS and the high-molecular-mass PAH/PAA. The adsorbed amounts of PAH and PDADMAC were also determined, showing a lower adsorbed amount of the low-molecular-mass PAH than of the high-molecular-mass PDADMAC. The amount of low-molecular-mass PDADMAC was similar to that found for high-molecular-mass PDADMAC/PSS. Individual fibers were partly treated and studied, showing a less significant decrease in wettability with low-molecular-mass PDADMAC/PSS than with the high-molecular-mass combination. The effect of the molecular weight on the adhesion was discussed in terms of the structure and wettability of the PEMs. [Copyright &y& Elsevier]

Abstract: Individual wood fibres were partly treated with polyelectrolyte multilayers (PEMs) consisting of two different polymer combinations, poly allylamine (PAH)/poly acrylic acid (PAA) and polyethylene oxide (PEO)/PAA in order to study the influence of these polymers on fibre wettability. Single fibres were partly treated and analysed using a so-called dynamic contact analyser (DCA) where the fibres are wet under controlled conditions. When PAH/PAA was used, a stronger influence on fibre wettability was detected when PAH was adsorbed in the outermost layer of the multilayer than when PAA was adsorbed in the outermost layer. The wettability of fibres treated with PAH/PAA PEMs was also influenced by the pH of the adsorption. With the PEO/PAA system, however, the type of polymer adsorbed in the outermost layer caused no detectable difference. Tests of sheets prepared from fibres treated with PEO/PAA showed an increase of about 90% in the tensile index when 9 layers were adsorbed. These and other recently published results from similar experiments using PAH/PAA [S.M. Notley, M. Eriksson, L. Wågberg, J. Colloid Interface Sci. 292 (2005) 29] are compared to the results for the PEM-treated individual fibres. The results indicate that fibres with low wettability contribute to greater paper strength. AFM-force measurements, with the aid of a colloidal probe technique, have also been performed using PAH/PAA, showing that there is also a close correlation between lower wettability of the surfaces and a higher pull-off force between the PEM treated surfaces, i.e. the flat surface and the colloidal probe. This is valid for the two pH strategies that are used for the formation for the PAH/PAA PEMs, which are studied using AFM-force measurements. [Copyright &y& Elsevier]

Abstract: Polydimethyldiallylammonium chloride (PDADMAC) and polystyrene sulfonate (PSS) have been used to build-up polyelectrolyte multilayers (PEMs) on chemical soft wood fibres and on SiO2 at various electrolyte concentrations. Adsorption onto SiO2 was studied using a stagnation point adsorption reflectometer (SPAR), and the adsorbed amount of PDADMAC and PSS on the fibres was determined using nitrogen analysis and Schöniger burning, respectively. The adsorption onto the two substrates was then compared. Paper testing showed that the tensile index (TI) increased by about 90% when 11 layers had been adsorbed, and that there was a correlation between the adsorbed amount and the increase in TI. It was also shown that the particular polymer present in the outermost layer significantly influenced the TI, and that PDADMAC produced a higher TI. A correlation between the adsorbed amount and the TI was also found. Individual fibres were partly treated with a PEM and analysed using a dynamic contact angle analyser (DCA) and environmental scanning electron microscopy (ESEM). [Copyright &y& Elsevier]