This work assesses six different agricultural residues with the aim of finding alternative raw materials for a soda semichemical pulping process: stems of bell and chili pepper ( Capsicum annuum ), broad bean ( Vicia faba ), asparagus ( Asparagus officinalis ), pea ( Pisum sativum ), and okra ( Abelmoschus esculentus ). Pulping yields higher than 60% (m/m) were obtained, except for pea stems (43%). The drainability of all the pulps, expressed as the Schopper-Riegler index (ºSR), had values of over 70 ºSR. The Kajaani analyses of the fibers showed acceptable fiber lengths in all cases (0.64–0.92 mm), but on average shorter than the lengths of pulps from a commercial fluting paper (Old corrugated Container, OCC), that was found to be 1.27 mm. Handsheets of paper were produced both with the pulps under study and with mixtures of these pulps with OCC pulp. Several properties were measured to assess the use of the new fibers in a paper for cardboard production. The property showing the greatest differences was the Gurley porosity, ranging from 25 mL/min (asparagus) to 1300 mL/min (broad bean). Of the six residues tested, the okra residue fiber showed better properties than the commercial paper fiber (Concora Medium Test indexes: 1.5 N m 2 /g and 1.1 N m 2 /g respectively, Burst Indexes: 2.3 kPa m 2 /g and 1.7 kPa m 2 /g, respectively), yielding similar mechanical properties to those of high quality fibers obtained from miscanthus ( Miscanthus giganteus ). Broad bean residue could also be a promising raw material, though its properties are not as good as okra’s. [ABSTRACT FROM AUTHOR]

In accordance with global estimations, approx. 15 million tons of residues are yearly generated from paper and pulp industry, which are traditionally used as biofuels or just disposed in landfills. However, residues composition and laws in force urge producers to search for new waste management strategies. From another point of view, the construction industry uses more than 33% of total natural resources, worldwide which has led several governments to limit the use of natural raw materials for building. In particular, fired brick industry produces yearly approx. 1600 billion bricks which represents millions of tons of natural resources consumption. Therefore, the goal is to contribute to reduce the amount of used clay. Thus, this paper explores the mineral and technological properties of brick made by using different percentages of paper pulp residues and fired at 900 °C. Results indicate that by increasing the replacement ratio, blend requires larger amounts of water which leads to a proportional increasing of shrinkage during drying. In spite of mineral transformations are not influenced by paper pulp residue, the porosity is linearly increased which leads to reduce compressive strength and thermal conductivity up to 30% for 20% of replacement ratio, in both cases. Thus, it is concluded that series made by replacing up to 10% show compressive strength above 5 MPa, water absorption beyond 20% and toxicity indexes meet the mandatory requirements. [ABSTRACT FROM AUTHOR]