Search

We have studied the decomposition of methanol-d4 on thin film Al2O3/NiAl(100) under near-ambient-pressure conditions, with varied surface-probe techniques and calculations based on density-functional theory. Methanol-d4 neither adsorbed nor reacted on Al2O3/NiAl(100) at 400 K under ultrahigh vacuum conditions, whereas they dehydrogenated, largely to methoxy-d3 (CD3O*, * denoting adsorbates) and formaldehyde-d2 (CD2O*), on the surface when the methanol-d4 partial pressure was increased to 10−3 mbar and above. The dehydrogenation was facilitated by hydroxyl (OH* or OD*) from the dissociation of little co-adsorbed water; a small fraction of CD2O* interacted further with OH* (OD*) to form, via intermediate CD2OOH* (CD2OOD*), formic acid (DCOOH* or DCOOD*). A few surface carbonates were also yielded, likely on the defect sites of Al2O3/NiAl(100). The results suggest that alumina not only supports metal clusters but also participates in reactions under realistic catalytic conditions. One may consider accordingly the multiple functions of alumina while designing ideal catalysts. [ABSTRACT FROM AUTHOR]

Pt and Rh nanoclusters, grown on deposition of Pt and Rh vapors onto graphene/Pt(111), show separate reactivity toward the decomposition of methanol-d4. The Pt (Rh) clusters had a mean diameter 2.0–3.5 nm (2.1–4.0 nm) and height 0.45–0.94 nm (0.41–0.9 nm) evolving with the coverage; they were structurally ordered, having an fcc phase and growing in (111) orientation, and had lattice constants similar to their bulk values. Methanol-d4 on the Pt clusters did not decompose but desorbed mostly, disparate from that on Pt(111) surface; the disparity arose as the adsorption energies of methanol-d4 on most surface sites of the Pt clusters became smaller than their single crystal counterpart. This size effect, nevertheless, did not apply on the Rh clusters, despite their similar atomic stacking; the Rh clusters showed a reactivity similar to that of the Rh(111) surface because the adsorption energies of methanol-d4 on both Rh clusters and Rh(111) are comparable. The distinct size dependence was rationalized through their electronic structures and charge distribution of Fukui function mapping. Our results suggest that reactive transition metals do not necessarily become more reactive while they are scaled down to nanoscale; their reactivity evolves with their size in a manner largely dependent on their electronic nature. [ABSTRACT FROM AUTHOR]

We have studied the decomposition of methanol-d4 on thin film Al2O3/NiAl(100) under near-ambient-pressure conditions, with varied surface-probe techniques and calculations based on density-functional theory. Methanol-d4 neither adsorbed nor reacted on Al2O3/NiAl(100) at 400 K under ultrahigh vacuum conditions, whereas they dehydrogenated, largely to methoxy-d3 (CD3O*, * denoting adsorbates) and formaldehyde-d2 (CD2O*), on the surface when the methanol-d4 partial pressure was increased to 10-3 mbar and above. The dehydrogenation was facilitated by hydroxyl (OH* or OD*) from the dissociation of little co-adsorbed water; a small fraction of CD2O* interacted further with OH* (OD*) to form, via intermediate CD2OOH* (CD2OOD*), formic acid (DCOOH* or DCOOD*). A few surface carbonates were also yielded, likely on the defect sites of Al2O3/NiAl(100). The results suggest that alumina not only supports metal clusters but also participates in reactions under realistic catalytic conditions. One may consider accordingly the multiple functions of alumina while designing ideal catalysts., (© 2023 Author(s). Published under an exclusive license by AIP Publishing.)