One of the most important elements of furnaces, boilers and other heating units is the structure (lining), usually made of silica–alumina, basic or special refractories. The basic refractories are materials that are increasingly in demand and whose manufacturing involves necessarily the use of MgO and CaO. In this article, the description and characterization of magnesite (MgCO3) and dolomite (Mg,Ca(CO3)2) and their contribution in industrial ceramics-refractories have been reviewed.

In this article, the elaboration and the characterization of silica-alumina refractory have been reviewed. Refractory oxides encompass a broad range of unary, binary, and ternary ceramic compounds that can be used in structural, insulating, and other applications. This paper provides a historical perspective on the elaboration and the use of silica-alumina refractory, reviews applications for refractory oxides, describes typical processing routes, overviews fundamental structure–property relations, and summarizes the properties of these materials.

Processing of mullite and alumina based refractory ceramic by unidirectional dry pressing, from two mixtures that include silica sand, pure alumina (PA) and recycled alumina (RA) is described. The samples were sintered up to 1600 °C to study the refractory properties. The fired properties of materials (firing shrinkage, water absorption, density, flexural strength, refractoriness, and SEM microstructure) were evaluated. Promising refractories materials based on mullite and alumina were obtained.

Refractory materials were elaborated from silica–alumina geomaterials related to granitoids and their direct surrounding rocks (kaolin clay and andalusite rich schist). The use of andalusite rich schist as aggregates (mean grain size: 1000–2000 μm) could improve the mechanical properties of synthesized refractory. The flexural strength increased from 39.10 to 54.16 MPa. The pyroscopic temperature increased from 1400 to 1450 °C. Thermal conductivity of the porous brick produced in this study (1.11 W/m K) showed 39% of reduction compared to initial brick of the same composition (1.83 W/m K). The thermal shock tests showed that the refractory samples have a good thermal shock resistance.