Y2Sr3B4O12 phosphors doped with europium ions were synthesized by a modified conventional solid-state reaction method. Characterizations of the prepared samples, viz., X-ray diffraction (XRD), scanning electron microscopy (SEM), photoluminescence (PL), and Commission Internationale de I'Eclairage were studied. The XRD analysis confirmed the formation of mixed phase due to polyborate and has a hexagonal crystalline yttrium orthoborate phosphor. SEM images showed the irregular morphology of the sample. The grain size distribution was broad and the average size was found to range from 2 μm to 100 nm. PL measurements showed excitation and emission characteristics of the prepared phosphor with different concentrations of the doping ion. From the emission spectra, it was clearly observed that the emission intensity of the magnetic dipole was higher than that of electric dipole transition owing to the Eu3+ ions occupying a higher symmetry site in the Y2Sr3B4O12 host. The intensity of PL increased with increasing concentration of the doping ion up to 2.0 mol.%; after that, the PL intensity decreased owing to the concentration-quenching phenomenon. The results indicated that Y2Sr3B4O12:Eu3+ phosphors can be selected as a potential candidate for solar cell/photovoltaic application. [ABSTRACT FROM AUTHOR]

We discuss new features of Sm3+-doped LaCePO4 phosphor as a potential candidate for display applications. Mainly, the traditional modified solid-state synthesis technique was used to prepare the samples. The X-ray diffraction technique was used for the structural studies. LaCePO4:Sm3+ phosphor production was verified by Fourier transform infrared studies. It was customary to use scanning electron microscopy to learn more about the morphology of the prepared samples. Additionally, photoluminescence (PL) analysis of the phosphor samples was presented for different doping ion concentrations with various excitations. In the presence of Sm3+, LaCePO4 emits powerful blue and orange emissions. In-depth research was carried out on the transitions between the concentration quenching effect and the doping ion. The distribution of the spectral region estimated from PL emission spectra was shown in the 1931 Commission International de l'Éclairage (x, y) chromaticity coordinates and was located (0.20, 0.22) in the blue region. According to our research, as-prepared phosphor may find useful application in display devices, especially because of its blue and orange content. [ABSTRACT FROM AUTHOR]