We report on photoluminescence (PL) properties of Er3+ doped Ga10Ge25S65 glass. Experiments were performed using 5 ns laser pulses at 980 nm (532 nm), in resonance with the 4I15/2→4I11/2 (4I15/2→2H11/2) transition of the Er3+ ions. PL bands were observed from the blue to the near-infrared and the dependence of their intensity as a function of the laser intensity was analyzed. The PL temporal behavior was analyzed through rate equations for the population densities and using the Inokuti-Hirayama model. The results allowed identification of the PL pathways and the characterization of energy transfer processes involving pairs of ions. [ABSTRACT FROM AUTHOR]

Optical properties of a neodymium (Nd3+) doped glass having composition based on the (Ga2S3)–(GeS2) system are reported. Transition probabilities, radiative lifetimes, and branching ratios related to Nd3+ levels were determined. Frequency upconversion (UC) luminescence due to nonresonant excitation at 1064 nm was observed at ≈535, ≈600, and ≈670 nm. The dependence of the UC intensity on the laser intensity and on the Nd3+ concentration as well as the dynamics of the luminescence process were studied. The results indicate that two-photon absorption by isolated Nd3+ ions and energy transfer among pairs of Nd3+ ions contribute to the UC luminescence. [ABSTRACT FROM AUTHOR]

We report on orange-to-blue frequency upconversion (UC) in Pr3+ doped chalcogenide glass (Ga10Ge25S65) doped with Ag2S and heat treated under different conditions to nucleate silver nanoparticles (NPs). The experiments were performed using 7 ns pulses from a dye laser that operates at ∼590 nm, in resonance with the 3H4→1D2 transition of Pr3+ ions. The enhancement observed in the UC emission at ∼494 nm, ascribed as 3P0→3H4 transition of the Pr3+ ion, is attributed to the large local field acting on the emitting ions due to the presence of the metallic NPs. [ABSTRACT FROM AUTHOR]

Several experimental studies are conducted to explain the different photoluminescence properties of the [Er.sup.3+] doped [Ga.sub.10][Ge.sub.25][S.sub.65] glass excited at 980 and 532 nm. The intensity of the system is shown to be highly dependent on the laser intensity of the films.

Optical properties of a neodymium ([Nd.sup.3+]) doped glass which bear composition based on the ([Ga.sub.2][S.sub.3])-(Ge[S.sub.2]) system are reported. The results indicated that two-photon absorption by isolated [Nd.sup.3+] ions and energy transfer among pairs of [Nd.sup.3+] ions contributed to the UC luminescence.

The experimental studies on orange-to-blue frequency upconversion (UC) in [Pr.sup.3+] doped chalcogenide glass ([Ga.sup.10][Ge.sup.25][S.sup.65]) doped with [Ag.sub.2]S and heat treated under different conditions to nucleate silver nanoparticles (NPs) is reported. The results shed light on the enhancement of the UC emission at ~494 nm, described as transition of the [Pr.sup.3+] ion which is attributed to the large local field acting on the emitting ions due to the presence of the metallic NPs.