The growth kinetics of ternary Co1−xNixSi2 thin films was studied in real time. The “Kissinger” method was applied to the results of ramped sheet resistance measurements to extract the apparent activation energy for the growth process. By simultaneously acquiring sheet resistance, x-ray diffraction and laser light scattering data on one hand and combining resistance measurements and Rutherford backscattering spectrometry on the other hand, we could distinguish between the initial, nucleation controlled thin film growth, and the subsequent diffusion controlled growth. The apparent activation energy for the initial growth decreases with increasing Ni concentration as a result of a lower nucleation barrier for the ternary disilicide. The markedly different microstructure of the ternary Co1−xNixSi2 films with respect to pure CoSi2 layers lies at the origin of a lower activation energy for the diffusion controlled growth of the ternary films. Despite the low activation energy, these films grow at a much slower...

We have studied the effect of the addition of Pt on the growth stress and thermal stress of NiSi films. Platinum was added in the form of an interlayer (Ni/Pt/Si), capping layer (Pt/Ni/Si), and as an alloying element within the as-deposited Ni film (Ni–Pt/Si). The evolution of film stress during the solid-state reaction was monitored using in situ curvature measurements. The large transient compressive growth stress observed during the reaction of pure Ni with Si was significantly reduced for samples with a Pt interlayer or alloy. Based on in situ XRD measurements, this reduction in the compressive growth stress could be related to the disappearance of Ni rich phases from the phase sequence and an overall increase in the silicidation temperature during ramp anneals. Pt was also found to affect the buildup of thermal stress while cooling down the sample after Ni1−xPtxSi formation. The presence of Pt as a solute in the monosilicide causes a significant increase in the stress relaxation temperature, and ther...

Mixed Co1-xNixSi2 films (0 = 50% Ni, the (100) orientation dominates the thin-film texture, due to the growth of a NiSi2-rich film at the substrate interface. The changing nucleation site, due to this phase separation, and the differing growth kinetics can significantly alter the texture of ternary films. These two factors should be taken into consideration when implementing ternary alloys in devices, since their physical properties, stability, roughness, resistance, etc., depend critically on the texture of the films. (C) 2008 American Institute of Physics. ispartof: Journal of Applied Physics vol:103 issue:6 status: published