Search

Quaternary sputtered TiAlSiN coatings were investigated for their high temperature structural stability, surface morphology, mechanical behaviors, surface chemical bonding states, solar absorptance and thermal emittance for possible solar selective surface applications. The TiAlSiN films were synthesized, via unbalanced magnetron sputtered technology, on AISI M2 steel substrate and annealed at 500 °C - 800 °C temperature range. SEM micrographs show nanocomposite-like structure with amorphous grain boundaries. Nanoindentation analyses indicate a decrease of hardness, plastic deformation and constant yield strength for the coatings. XPS analysis show mixed Ti, Al and Si nitride and oxide as main coating components but at 800 °C the top layer of the coatings is clearly composed of only Ti and Al oxides. Synchrotron radiation XRD (SR-XRD) results indicate various Ti, Al and Si nitride and oxide phases, for the above annealing temperature range with a phase change occurring with the Fe component of the substrate. UV–Vis spectroscopy, FTIR spectroscopy studies determined a high solar selectivity, s of 24.6 for the sample annealed at 600 °C. Overall results show good structural and morphological stability of these coatings at temperatures up to 800 °C with a very good solar selectivity for real world applications. [ABSTRACT FROM AUTHOR]

Chromium nitride (CrN)-based materials display broad applications as protective coatings for automotive, power generation and aerospace industries, in which surfaces are often subjected to wear and corrosion. By using an appropriate choice of dopant, one can further increase the mechanical hardness, corrosion and oxidation resistance of these coatings. In order to identify the effect of dopants on the structural evolution and surface electronic properties of CrN coatings, Cr 1- z (Al/Si) z N coatings were prepared by magnetron sputtering and then characterized via X-ray diffraction (XRD) and soft X-ray synchrotron radiation Near-edge X-ray Absorption Fine Structure (NEXAFS) studies around N K -edge. Higher degree of crystallinity of the coatings were identified through XRD studies. The bonding structure, of the doped CrN coating, was analyzed by Near-edge X-ray Absorption Fine Structure (NEXAFS) measurements performed around the N K -edge (390–450 eV) in the Auger electron yield (AEY) and total fluorescence yield (TFY) modes. NEXAFS analysis revealed Cr 3d (Al3 p /Si3 p )N2 p hybridizations in Cr 1- z (Al/Si) z N compositions and complex structure splitting via spin–orbit interaction of the Cr3 d levels. [ABSTRACT FROM AUTHOR]

Sol-gel derived CuCo-oxide coatings as solar selective surfaces, synthesized onto aluminium substrates at various annealing temperatures, are analysed by correlating their structural, chemical bonding states, and surface morphological topographies. As the annealing progressed, all the coatings displayed a Cu 0.56 Co 2.44 O 4 (ICSD 78-2175) phase with preferential orientation along (400) reflection plane. Rietveld refinement of X-ray diffraction (XRD) data indicate that residual stress and microstrains developed around the coating surfaces are reduced resulting in mechanically stable thin films. Enhancement of the crystallite size and preferred orientation of the surface were confirmed via XRD, field emission scanning electron microscopy (FESEM), and atomic force microscopy (AFM) analysis. X-ray photoelectron spectroscopy (XPS) analysis shows tetrahedral, octahedral and mixed states of Cu and Co ions with a stable atomic ratio of Co/Cu, and an increase of O and C contents but no metal-carbon bonding on the surface of materials. Optical reflectance investigations indicated that solar selectivity of the coatings increased from 3.81 to 24 as the annealing temperature reached up to 500 °C. [ABSTRACT FROM AUTHOR]

Highlights: [•] Al or Si is doped on CrN and AlN coatings using magnetron sputtering system. [•] NEXAFS analysis is conducted to measure the Al and Si K-edges, and chromium L-edge. [•] Structural evolution of CrN matrix with addition of Al or Si element is investigated. [ABSTRACT FROM AUTHOR]

Abstract The temperature dependence of phase composition and lattice parameters, for TiAl x N thin film coating, are experimentally investigated by in-situ synchrotron radiation X-ray diffraction (SR-XRD), at temperatures between 25 °C and 700 °C. Mechanical properties, such as: Young's modulus (E), hardness (H) and plastic deformation index (PDI) – were experimentally determined by nanoindentation, at 25 °C. Crystalline structural analysis, of SR-XRD results, indicates the major phases are TiN and AlN; with Ti 2 O and TiO 2 phases also present above 600 °C. The lattice constants increased with an increase in temperature. Atomic and phase compositions, at 25 °C, were also verified by X-ray photoelectron spectroscopy (XPS). Field emission scanning electron microscopy (FESEM) images display an increase in surface roughness and reduction in grain size, with increasing Aluminium percentage (Al%). Nanoindentation analysis showed a maximum hardness of 25.1 ± 1.5 GPa (sample containing 12% Al), which was subsequently reduced upon addition of more Aluminium. Finite element modelling (FEM), including von Mises stress distribution, indicates lower mechanical integrity, for samples with high Al% content. Highlights • Hardness increase upon the addition of small amounts of Aluminium doping. • Significant increase in resistance of plastic deformation with increasing doping. • High temperature in-situ analysis detected an increase in lattice parameters. • Film coatings with different doping exhibited different oxidation states. • Finite element modelling evaluated mechanical integrity of films under load. [ABSTRACT FROM AUTHOR]

Chromium nitride (CrN) coatings were deposited by magnetron sputtering onto Si(100) substrates. The coatings were then annealed at different temperatures (500–800 °C in steps of 100 °C) in air for 1 h. X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), X-ray photoelectron spectroscopy (XPS), UV–Vis spectroscopy, nanoindentation tests and finite element modeling (FEM) were conducted in order to investigate their structural, morphological, optical and mechanical properties. XRD patterns show that the crystallinity of the CrN phase increases with the rise in annealing temperatures together with its preferred orientations along (111) and (200) diffraction planes. The lattice constants were slightly reduced from 4.19 to 4.11 nm at 800 °C. The lattice micorstrains and residual stresses were also reduced as the annealing temperatures rose as a result of reduced defects, dislocations and vacancies. Smooth grain-like surfaces with grain sizes ranging between ∼50 and 250 nm were confirmed by FESEM micrographs. XPS studies indicated the existence of Cr and N on the coating systems. Optical studies showed that with the rise in annealing temperature of up to 700 °C, the solar absorptance of CrN coatings is increased from 61% to 89% and slightly decreased at 800 °C, while the optical band-gap energy dropped from 2.62 to 1.38 eV and slightly increased to 1.48 eV at 800 °C. A gradual increase of dielectric constants of CrN films were realized with the subsequent annealing progression. Nanoindentation results indicated that as the annealing progresses, the hardness and elastic modulus values are lowered. [ABSTRACT FROM AUTHOR]

Titanium-doped indium tin oxide thin films were synthesized via a sol-gel spin coating process. Surface chemical bonding states and mechanical properties have been investigated as a function of titanium content (2 and 4 at%) and annealing temperature ranging from 400 to 600 °C with increments of 100 °C. Raman analysis was performed to study the phonon vibrations for the prepared samples and the results revealed the existence of ITO vibrational modes. The elemental compositions, bonding states and binding energies of the film materials were investigated using X-ray photoelectron spectroscopy (XPS) technique. The XPS results indicated that the ratio of the metallic elements (In, Sn, Ti) to the oxygen on the surface of the thin film coatings decreased due to the increase of the oxide layer on the surface of the thin films. Also, by increasing the annealing temperature up to 600 °C, the Ti 2p and Cl 2p signals were no longer detected for both 2 and 4 at% Ti contents, respectively, due to the thicker surface oxidation layer. Mechanical properties of the synthesized films were also evaluated using a nanoindentation process. Variations in the hardness ( H ) and the elastic modulus ( E ) were observed with different Ti at% and annealing temperatures. The hardness is within the range of 6.3–6.6 GPa and 6.7–6.8 GPa for 2 and 4 at% Ti content samples, respectively, while the elastic modulus is within the ranges of 137–143 and 139–143 GPa for 2 at% and 4 at% Ti contents samples, respectively. A combination of the highest H and E were achieved in the sample of 4% Ti content annealed at 600 °C. Furthermore, the H/E ratio ranges from 4.5 × 10 −2 to 5.0 × 10 −2 which reflects a reasonable level of wear resistance. [ABSTRACT FROM AUTHOR]

Abstract: Cubic α-Fe2O3 (hematite) microparticles (side lengths=0.3–1.3μm) have been synthesized using glycine and ferric chloride via a simple one-step hydrothermal reaction. Their morphological, mineralogical and surface properties have been determined using scanning electron microscopy (SEM), atomic force microscopy (AFM), X-ray diffractometry (XRD) and X-ray photoelectron spectroscopy (XPS). XRD analysis indicated that the synthesized α-Fe2O3 microparticles were minerallogically pure. An increase in hydrothermal reaction duration from 10 to 24h increased the atomic percentages of α-Fe2O3 on the surface of the microparticles by almost 8%. The mechanism concerning reactions of species to produce this microparticles precipitate was elucidated based on thermodynamics and ionic equilibrium aspects. In the electrochemical analysis, the synthesized α-Fe2O3 microparticles (as cathode material) exhibit an approximate charge capacity of 160mAh/g and excellent coulombic efficiency of 94%. [Copyright &y& Elsevier]