Search

The (micron[m]+submicron[s]+nano[n]) SiC particles (SiCp) reinforced AZ31B magnesium matrix composites (AZ31B/SiCp/m + s + n composites) were fabricated by stirring casting technology followed by hot extrusion. This method has successfully solved the homodisperse problem of SiCp/m + s + n in the magnesium matrix composites. The influence of SiCp/m + s + n on the dynamic recrystallization (DRX) behavior of the magnesium matrix was investigated by researching the TEM microstructures of composites. The results indicated that the addition of SiCp/m + s + n was helpful to increase the ratio of DRXed nucleation and reduce the average grain size of matrix. The particle deformation zone (PDZ) can be formed in the vicinity of micron SiCp, while the region with high dislocation density can be created around submicron SiCp owing to pin dislocation and deformation mismatch between matrix and particles. These regions are ideal sites for the formation of recrystallization nucleus. Meanwhile, the addition of fine SiCp(nano and submicron) may delay or hinder the growth of matrix grain through the pinning effect on the grain boundaries during hot extrusion. The tensile test indicates that the strength of the AZ31B/SiCp/m + s + n composites has a significant improvement. Compared with the single sized or bimodal sized particles reinforced magnesium matrix composites, the tensile strength of the AZ31B/SiCp/m + s + n composites were highlighted. [ABSTRACT FROM AUTHOR]

A particulate reinforced magnesium matrix nanocomposite was subjected to multidirectional forging (MDF). The results showed that the microstructure of the nanocomposite mainly consisted of some large initial grains and fine recrystallized grains along initial grain boundaries after 1 MDF pass. With increasing the MDF passes, the degree of dynamic recrystallization increased and ultrafine grains with average size of about 20 nm were observed in the nanocomposites after 6 MDF passes. The distribution of SiC nanoparticles in the nanocomposite was homogeneous outside some SiC nanoparticle dense zones after different MDF passes. Compared with typical basal texture obtained for 1 MDF pass, the basal pole intensity decreased firstly for 3 MDF pass and then increased for 6 MDF passes. Both ultimate tensile strength and elongation to fracture of the nanocomposite were enhanced with increasing the MDF passes, while yield strength decreased after 3 MDF passes and then increased slightly after 6 MDF passes. [ABSTRACT FROM AUTHOR]

The present study dealt with the AZ91 alloy subjected to multidirectional forging (MDF) under decreasing temperature conditions with emphasizing on relationship between microstructures and mechanical properties generated by MDF. The obtained results showed that grains of the alloy were gradually refined while the amount of the second phase precipitated along the grain boundaries was increased with increasing the MDF passes and decreasing the MDF temperature. Compared with the as-cast alloy, yield strength, ultimate tensile strength and elongation of the AZ91 alloy after MDF under decreasing temperature conditions were simultaneously increased. As the numbers of MDF passes were gradually increased and the MDF temperature was gradually decreased, the yield strength was gradually decreased, suggesting that texture softening may overwhelm the strengthening due to the grain refinement as well as the homogeneous distribution of precipitates. [ABSTRACT FROM AUTHOR]

Highlights: [•] Friction stir processing (FSP) was applied to Mg–Gd–Y–Zn–Zr casting. [•] The grain boundary Mg3RE and LPSO phases in the casting dissolved after FSP. [•] Fine grains with LPSO phase distributed only within the grains was achieved. [•] High mechanical properties were obtained in FSP Mg–Gd–Y–Zn–Zr. [ABSTRACT FROM AUTHOR]

Abstract: In this research, the as-cast and as-homogenized Mg–8.2Gd–3.8Y–1.0Zn–0.4Zr alloy were subjected to the hot rolling with the same processing parameters. The microstructure and mechanical properties of the two kinds of as-rolled sheets were investigated. The sheet rolled from the as-cast alloy was mainly composed of recrystallized α-Mg grains surrounded by Mg3(Gd,Y) eutectic compounds. While the sheet rolled from the as-homogenized alloy was composed of large deformed grains with long-period stacking ordered (LPSO) phase inside and fewer recrystallized α-Mg grains, and exhibited higher strength due to the deformed grains with stronger basal texture and larger volume fraction of long-period stacking ordered (LPSO) phase. [Copyright &y& Elsevier]

Abstract: Mg–8.2Gd–3.8Y–1.0Zn–0.4Zr alloy sheets containing long period stacking ordered (LPSO) phase were prepared by hot rolling at 400°C with total reduction of 96%. Microstructure evolution of the sheets during hot rolling was investigated, and its influence on mechanical properties was discussed. Twinning occurred during the early stage of hot rolling, and disappeared after total reduction higher than 89%. Average grain size was gradually refined, microstructure became much more homogeneous and volume fraction of LPSO phase decreased with increasing rolling reduction. Furthermore, the type of LPSO phases far from and near the block shaped phases were identified to be different. Basal texture was obtained during rolling process, but the intensity declined with the further rolling, which is mainly due to the dynamic recrystallization and the addition of RE elements. The as-rolled sheet with 96% reduction shows excellent mechanical properties: yield strength of 318MPa, ultimate tensile strength of 403MPa and elongation to failure of 13.7% at ambient temperature along the rolling direction. [Copyright &y& Elsevier]