Search

Abstract: Magnesium matrix composite reinforced by graphite particles was fabricated using stir casting with graphite particle size of 50μm and graphite particle volume fraction of 10%. The as-cast composite was extruded at 250°C, 300°C and 350°C with an extrusion ratio of 12:1. The experimental results reveal that the extrusion temperature plays an important role on the microstructures and damping capacities. The aspect ratio of graphite particles increases as the extrusion temperature rises. Extrusion at 300°C leads to the highest damping values in low strain region at room temperature. It also demonstrates the highest damping values at elevated temperatures when the strain is 4×10−5. In addition, there are two definite damping peaks in the damping-temperature curves which occur at about 150°C and 350°C, respectively. [Copyright &y& Elsevier]

Abstract: In the present study, AZ91 magnesium matrix composites reinforced with six volume fractions (0.5, 1, 1.5, 2, 3 and 5vol.%) of submicron-SiC particulates (0.2μm) were fabricated by stir casting. The as-cast ingots were forged at 420°C with 50% reduction, and then extruded at 370°C with the ratio of 16 at a constant ram speed of 15mm/s. The microstructure of the composites was investigated by optical microscopy, scanning electron microscope and X-ray diffractometer. Microstructure characterization of the composites showed relative uniform reinforcement distribution, significant grain refinement and presence of minimal porosity. The X-ray diffractometer analysis showed that a strong basal plane texture was formed in both AZ91 alloy and SiCp/AZ91 composites during extrusion and the addition of submicron-SiC particulates could weaken the basal plane texture. The presence of submicron-SiC particulates assisted in improving the thermal stability, micro-hardness, elastic modulus and 0.2% yield strength. Both of the 0.2% yield strength and ultimate tensile strength increased with the increasing of submicron-SiC particulate content, however, decreased as the SiC particulate content overrun 2vol.%. [ABSTRACT FROM AUTHOR]

Carbon nanotubes (CNTs) reinforced magnesium matrix composite prepared by an improved process was extruded at 350°C with an extrusion ratio of 20:1. Most CNTs were individually and uniformly dispersed in the as-cast and the as-extruded composites. Moreover, good interfacial bonding was achieved, and Raman spectroscopy showed that the damage to CNTs was insignificant. The addition of CNTs could weaken basal plane texture. Meanwhile, the CNTs evidently improved the ultimate tensile strength, yield strength and Young's modulus of the as-extruded composite. Pulling-out CNTs proved that the length of the CNTs was not large enough to be compatible with the high strength of the CNTs. Grain refinement, load transfer mechanism and Orowan strengthening mechanism play important roles on the increase of the yield strength. The composites fabricated by our process showed high strengthening efficiency of CNTs. [ABSTRACT FROM AUTHOR]

The (micron[m]+submicron[s]+nano[n]) SiC particles (SiCp) reinforced AZ31B magnesium matrix composites (AZ31B/SiCp/m + s + n composites) were fabricated by stirring casting technology followed by hot extrusion. This method has successfully solved the homodisperse problem of SiCp/m + s + n in the magnesium matrix composites. The influence of SiCp/m + s + n on the dynamic recrystallization (DRX) behavior of the magnesium matrix was investigated by researching the TEM microstructures of composites. The results indicated that the addition of SiCp/m + s + n was helpful to increase the ratio of DRXed nucleation and reduce the average grain size of matrix. The particle deformation zone (PDZ) can be formed in the vicinity of micron SiCp, while the region with high dislocation density can be created around submicron SiCp owing to pin dislocation and deformation mismatch between matrix and particles. These regions are ideal sites for the formation of recrystallization nucleus. Meanwhile, the addition of fine SiCp(nano and submicron) may delay or hinder the growth of matrix grain through the pinning effect on the grain boundaries during hot extrusion. The tensile test indicates that the strength of the AZ31B/SiCp/m + s + n composites has a significant improvement. Compared with the single sized or bimodal sized particles reinforced magnesium matrix composites, the tensile strength of the AZ31B/SiCp/m + s + n composites were highlighted. [ABSTRACT FROM AUTHOR]