Search

• The effects of Sc, Y and Zr on the performances and microstructure evolution of Al-0.7Mg-0.6Si-0.2Ce alloys were studied. • An excellent combination of strength, elongation and electrical conductivity was achieved with the addition of Sc and Y. • The strengthening and electrical resistance mechanism of the studied alloys were revealed by statistical calculation. [Display omitted] In order to achieve the compatibility between excellent mechanical properties and good electrical conductivity of Al-Mg-Si alloys, detailed investigation was carried out to understand the microstructure evolution and their influences on performances of different Al-0.7Mg-0.6Si-0.2Ce-X (X Sc, Y and Zr) alloys prepared by casting, homogenization, hot extrusion, solution and aging treatments. Under aging state, Ce can form a large number of micron-sized AlCeSi and a few AlCeFeSi phase. The strength increased to 334 MPa as a result of decreased grain size and improved precipitation effect and the electrical conductivity increased up to 53.53%IACS because of lower solute Si atoms. The β" precipitates were coarsened and consequently the volume fracture was largely reduced due to the presence of Sc element, leading to the decreased strength of 311 MPa. The more solute Mg, Si and Sc atoms increased the degree of free electron scattering and the electrical conductivity decreased to 51.86%IACS. It is also found that Sc significantly enhanced the elongation of the alloy from 11.8% to 18.0%, which might be attributed to the formation of Al 3 Sc and (Al, Si) 3 Sc phases. The addition of Y raised the electrical conductivity of Al-Mg-Si-Ce alloy to 55.79%IACS by ameliorating the volume fraction and distribution of β" precipitates and decreasing the solute Si atoms. The co-addition of Sc and Y inherited the advantages of such two alloys. The ultimate tensile strength, elongation, electrical conductivity of Al-0.7Mg-0.6Si-0.2Ce-0.2Sc-0.1Y alloy processed by aging treatments is 336 MPa, 19.4% and 53.11%IACS, respectively. [ABSTRACT FROM AUTHOR]

The effects of trace Sc and Y on the corrosion behaviors of cold-drawn Al-0.2Ce alloys were revealed by scanning Kelvin probe force microscopy (SKPFM), transmission electron microscopy (TEM), scanning electron microscopy (SEM), Electron Probe Micro-analyzer (EPMA), and electrochemical measurements. The results showed that the Al 3 Sc particles not only enable the increase of subgrain boundaries in the modified alloy after cold drawing but also improve the morphology and size of the Al 13 Fe 3 Ce phase. SKPFM analysis showed that the enrichment of Y around the Al 13 Fe 3 Ce phase in the modified alloy can decrease its electrochemical inertness and thus reduce the micro-galvanic corrosion susceptibility of the alloy. The results of the electrochemical analysis showed that the individual and composite addition of Sc and Y can improve the corrosion resistance of the cold-drawn Al-0.2Ce alloy. The corrosion potential and current of Al-0.2Ce-0.2Sc alloy are −0.892 V and 0.91 μA·cm−2, while the corrosion potential and current of Al-0.2Ce-0.1Y alloy are −0.918 V and 1.08 μA·cm−2, respectively. It is obvious that Sc element improves the corrosion resistance of Al-0.2Ce alloy more effectively than Y element. The corrosion depth of Al-0.2Ce-0.2Sc-0.1Y alloy was the smallest tested by immersion under the same conditions, and its corrosion potential and corrosion current were −0.842 V and 0.79 μA·cm−2, respectively, corresponding to the best corrosion resistance. The formal mechanism of pitting corrosion in the alloys is also discussed. [Display omitted] • Effect of Sc on microstructure and corrosion of Al-0.2Ce alloy was revealed. • The enrichment of Y atoms around Al 13 Fe 3 Ce can reduce the potential difference. • The corrosion behaviors of pitting corrosion induced by Al 13 Fe 3 Ce was discussed. • The equivalent circuit of the studied alloys was identified. [ABSTRACT FROM AUTHOR]