Search

Dynamic mechanical properties of the selected laser melting (SLM)-NiCrFeCoMo 0.2 high-entropy alloy (HEA) are further improved by controlling the molten pool structure and the generation of σ-phase precipitation particles. In this study, a split Hopkinson pressure bar (SHPB) was used for testing the dynamical mechanical properties of the quenched SLM-NiCrFeCoMo 0.2 HEA specimens. Microstructure and volume fraction of the σ precipitates were characterized by X-ray diffractometry (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM), and the small angle neutron scattering (SANS) technique. After heating to 800 ℃, holding for 8 h and water quenching, the molten pool boundary of the SLM-NiCrFeCoMo 0.2 HEA disappear, and the ultimate compressive strength and the impact energy of specimens reach 1970 MPa and of 217.45 MJ·m−3, respectively. Due to the segregation of Mo elements in the molten-pool boundary of the as-build SLM-NiCrFeCoMo 0.2 HEA, more σ precipitates tend to form at the residual molten pool boundary of the quenched SLM-NiCrFeCoMo 0.2 HEA. The σ precipitates play key role in strengthening of the SLM-NiCrFeCoMo 0.2 HEA. • Annealed SLM- NiCrFeCoMo 0.2 HEA has larger ultimate compressive strength and the impact energy. • Lots of σ precipitates generate at the residual molten pool boundary. • Small angle neutron scattering technique is used to analyze the volume fraction of σ precipitates. • The σ precipitates play key role in strengthening of the SLM-NiCrFeCoMo 0.2 HEA. [ABSTRACT FROM AUTHOR]

A cost-effective iron-rich non-equiatomic Fe 50 Mn 20 Al 15 Ni 10 Co 5 medium entropy alloy (MEA) was synthesized by vacuum induction melting. The as-cast alloy exhibits a multiphase microstructure with the ordered B2 (a= 2.90 ± 0.01 Å), disordered body-centred cubic (BCC) (a= 2.89 ± 0.01 Å) and face-centred cubic (FCC) (a= 3.61 ± 0.02 Å) phases. X-ray diffraction (XRD) and transmission electron microscope (TEM) were used to confirm the structure of the evolved phases. The columnar dendrites having a width in the range of 120–300 µm were observed in the as-cast structure. The formation of Ni-Al rich B2 precipitates in the BCC matrix was confirmed based on detailed microstructural characterization using scanning electron microscope (SEM) and TEM. The phase separation in the form of modulated structure of ordered B2 and disordered BCC phase was related to the spinodal decomposition. The formation of the FCC phase at and near the grain boundaries is linked to simultaneous nucleation and growth mechanisms, which occur during the solidification. The as-cast alloy has shown an average compressive yield strength of ∼1250 MPa and ultimate strength of ∼1675 MPa, along with a compressive strain of ∼42%. The optimum balance of strength and ductility is achieved due to the formation of the hard (B2, BCC) and soft (FCC) phases and their interplay during the deformation process. These encouraging results of the alloy in the as-cast state have provided the direction to design and develop such economically viable alloys, which could be produced at industrial scale. • A novel cost-effective Fe 50 Mn 20 Al 15 Ni 10 Co 5 MEA was synthesized by vacuum induction melting. • Alloys exhibits two phase structure of BCC and FCC in as-cast state. • The modulated structure of B2 and BCC was related to spinodal decomposition. • The optimum balance of strength and ductility is achieved in the alloy. [ABSTRACT FROM AUTHOR]

As-explosive welded clad plates usually show poor ductility due to heavily deformed microstructures developed after explosive welding (EXW). In this study, the feasibility of improving mechanical properties of an EXWed Mg–6Al–1Zn–1Ca (AZX611)/Al–0.6Mg–0.6Si–0.1Fe (A6005C) (all in wt%) clad plate has been explored by subsequent hot-rolling. Increasing the thickness reduction per pass from 10% to 28% or decreasing the rolling temperature from 430 °C to 250 °C is shown to enhance tensile properties. The joint sheet rolled at 250 °C with a thickness reduction per pass of 28% shows a large fracture elongation of 15%, which is significantly higher than that of the as-EXWed clad plate, 1.2%. Microstructure characterization by means of scanning electron microscope, electron backscatter diffraction and transmission electron microscope reveals that the substantial improvement in ductility is intimately related to a significant reduction of the accumulated strain in AZX611 and A6005C alloy sheets and an elimination of the interface delamination formed during EXW. A certain degree of anisotropic mechanical properties is observed in all sheets regardless of rolling conditions, which can be ascribed to the mechanical anisotropy originated from the AZX611 and A6005C alloy sheets. • Producing high performance lightweight Mg/Al joint sheets by explosive welding followed by conventional hot rolling. • Characterizing microstructure and evaluating mechanical properties of EXWed Mg/Al joint sheets rolled in different conditions. • Providing an in-depth understanding of the relationship between rolling condition, microstructure and mechanical properties. [ABSTRACT FROM AUTHOR]