Introducing nanoparticles onto the surface of carbon fibers (CFs) is a useful method for enhancing the quality of fiber-matrix interface. In this work, a liquid sizing agent containing functionaliz...

The multi-scale reinforcement and interfacial strengthening on carbon fiber (CF)-reinforced methylphenylsilicone resin (MPSR) composites by adding silica-coated multi-walled carbon nanotubes (SiO2-CNTs) were investigated. SiO2-CNT has been successfully prepared via the hydrolysis of tetraethoxysilane in the presence of acid-oxidized multi-walled carbon nanotubes. Transmission electron microscopy, X-ray diffraction, and Fourier Transform infrared spectroscopy were carried out to examine the functional groups and structures of CNTs. Then, SiO2-CNT was incorporated into MPSR matrix to prepare CF/MPSR-based composites by the compression molding method. The effects of the introduced SiO2-CNT on the interfacial, impact, and heat-resistant properties of CF/MPSR composites were evaluated by short-beam bend method, impact test, and thermal oxygen aging experiments, respectively. Experimental results revealed that the CF/MPSR composites reinforced with 0.5 wt% SiO2-CNT showed a significant increase 34.53% i...

A liquid sizing agent containing multiwall carbon nanotubes (MWCNTs) was prepared for carbon fiber (CF) reinforced methylphenylsilicone resin (MPSR) composite applications. In order to improve the dispersion of MWCNTs in the sizing agent and interfacial adhesion between CF and MPSR, MWCNTs and CF were functioned by the chemical modification with tetraethylenepentamine (TEPA) used as a MPSR curing agents. The CF before and after the sizing treatment-reinforced MPSR composites were prepared by a compression molding method. The microstructures, interfacial properties, and impact toughness of CF were systematically investigated. Experimental results revealed that a thin layer of MPSR coating containing functionalized MWCNTs (MWCNT-TEPA) was uniformly grafted onto the surface of CF. The sized CF-reinforced MPSR composite showed simultaneously remarkable enhancement in the interlaminar shear strength and impact toughness. Meanwhile, the tensile strength of CF had no obvious decrease after sizing treatment. In a...

The performance of carbon fibers-reinforced composites is dependent to a great extent on the properties of fiber–matrix interface. To improve the interfacial properties in carbon fibers/epoxy composites, nano-SiO2 particles were introduced to the surface of carbon fibers by sizing treatment. Atomic force microscope (AFM) results showed that nano-SiO2 particles had been introduced on the surface of carbon fibers and increase the surface roughness of carbon fibers. X-ray photoelectron spectroscopy (XPS) showed that nano-SiO2 particles increased the content of oxygen-containing groups on carbon fibers surface. Single fiber pull-out test (IFSS) and short-beam bending test (ILSS) results showed that the IFSS and ILSS of carbon fibers/epoxy composites could obtain 30.8 and 10.6% improvement compared with the composites without nano-SiO2, respectively, when the nano-SiO2 content was 1 wt % in sizing agents. Impact test of carbon fibers/epoxy composites treated by nano-SiO2 containing sizing showed higher absorpt...