This study systematically investigates the effect of Shear Thickening Fluid (STF) treatment on the high strain rate properties of UHMWPE (Ultra High Molecular Weight Poly Ethylene) composites. Spherical nanosilica particles of size 100 nm were used for the synthesis of STF. The high strain rate impact studies were accomplished on in-house designed and fabricated Split Hopkinson Pressure Bar (SHPB) experimental set-up. Compression moulded UHMWPE variant Gold Shield ® was used as the ballistic composite. Both STF-treated as well as neat Gold Shield ® specimens were subjected to high strain rate impact testing. From the experimental results and Fractography studies it was revealed that STF treatment enhanced the ballistic resistance of Gold Shield ® composite material. In the SHPB experiments, the improved ballistic performance of STF-treated Gold Shield ® specimens was manifested in terms of higher peak stress, specimen strain rates and impact toughness. [ABSTRACT FROM AUTHOR]

Shear thickening fluids (STFs) are a special class of field responsive fluids which exhibit change of phase from liquid to solid when subjected to imposed shear. This remarkable characteristic of STFs has led to their application in soft body armor technologies, leading the development of concept of Liquid Body Armors (LBAs). LBAs extensively rely upon the symbiotic relationship between STF and high strength FRP (Fiber Reinforced Polymer) composites comprising of high tenacity fibers such as Kevlar, UHMWPE (Ultra High Molecular Weight Poly Ethylene) etc. Although in the past, STFs have been widely characterized by rheometers at low strain rates (≤10 3 s −1 ), but in actual practical scenarios, body armours encounter much higher strain rates (of the order of 10 5 –10 7 s −1 ) under a ballistic impact. The main objective of this study is to capture the dynamics of STFs at such high strain rates by employing Split Hopkinson Pressure Bar (SHPB) technique. The STF sample was synthesized by dispersing 67.5 wt.% of 100 nm silica powder in Poly Propylene Glycol (PPG) and ethanol, using ultrasonic homogenization method. The mechanical response of STF was studied at high strain rates in terms of the stress-strain behavior and variation of the impact toughness with the loading rate of the fluid specimen. It was observed that the impact toughness of STF increased progressively with the specimen loading rate. The peak stress and peak strain rate attained in the SHPB tests were 147 MPa and 22,100 s −1 , respectively. The characteristic transition time of STF was found to be in the range of 13–25 µs. [ABSTRACT FROM AUTHOR]