Search

A high-performance self-humidifying membrane electrode assembly (MEA) was prepared by inserting hygroscopic microcrystalline cellulose (MCC) between the gas diffusion layer (GDL) and the catalyst layer (CL). At low humidity, the MEA exhibited good self-humidification, including high output and good stability. With our optimal MEA, in which the MCC loading was ca. 0.5 mg cm −2 , the current density at 0.6 V reached 1100 mA cm −2 and the maximum power density was 751 mW cm −2 , at a relative humidity (RH) of 30% for both anode and cathode gases and a cell temperature of 70 °C; the performance was comparable to that of a MEA prepared without added MCC and operated at 100% RH. Further, after 24 h of operation at low humidity and 0.6 V, the MEA's current density decreased by only 9.1%, compared with the 60% decline experienced by the MEA without MCC after 3 h under the same conditions, demonstrating the former's good self-humidification stability. When we attempted to insert the MCC layer elsewhere, including between the membrane and the anode CL, we found that inserting it between the GDL and the anode CL yielded the best performance. The high self-humidification performance of this MEA is attributable to the strong wettability and water-retention capacity of MCC. The MCC layer between the GDL and the anode CL ensured the latter would remain sufficiently wet and accelerated hydrogen activation and proton transfer, resulting in the MEA having high self-humidification under conditions of low humidity and high cell temperature. [ABSTRACT FROM AUTHOR]

Pd@Pt nanoparticles with a three-dimensional (3D) nanospherical shape have been prepared using a two-step approach in which the Pd nanospheres are synthesized controllably by a solvothermal method, and then a Pt monolayer is deposited on the Pd nanospheres using an underpotential deposition process. We systematically investigate (i) the influences of temperature and additive on the morphology of the Pd nanoparticles and (ii) the electrochemical activity of Pd@Pt for the oxygen reduction reaction (ORR). The Pd@Pt nanoparticles exhibit enhanced activity towards the ORR. The mass activity of Pt in the Pd@Pt nanospheres (1.03 A mgPt −1 ) is 3.3 times higher than that of commercial Pt/C (0.24 A mgPt −1 ). The catalyst enhanced activity may result from the 3D structure of the Pd nanospheres and the monolayer dispersion of Pt on the surface of the nanoparticles. [ABSTRACT FROM AUTHOR]

Abstract: In this work, a membrane electrode assembly (MEA) for proton exchange membrane fuel cell (PEMFC) operating under no external humidification has been successfully fabricated by using a composite Pt/SiO2/C catalyst at the anode. In the composite catalyst, amorphous silica, which originated from the hydrolysis of tetraethyl orthosilicate (TEOS), was immobilized on the surface of carbon powder to enhance the stability of silica and provide a well-humidified surrounding for proton transport in the catalyst layer. The characteristics of silica in the composite catalyst were investigated by XRD, SEM and XPS analysis. The single cell tests showed that the performance of the novel MEA was comparable to MEAs prepared using a standard commercial Pt/C catalyst with 100% external humidification, when both were operated on hydrogen and air. However, in the absence of humidification, the MEA using Pt/SiO2/C catalyst at the anode continued to show excellent performance, while the performance of the MEA containing only the Pt/C catalyst rapidly decayed. Long-term testing for 80 h further confirmed the high performance of the non-humidified MEA prepared with the composite catalyst. Based on the experimental data, a possible self-humidifying mechanism was proposed. [ABSTRACT FROM AUTHOR]

Abstract: By using two non-ionic surfactants, 1,12-diaminododecane and a triblock copolymer surfactant F127, as templates, grape-like solid spheres of super-microporous silica (SMS) with ordered, worm-like pore structures have been successfully synthesized, then characterized by SEM/TEM, XRD, TG/DTA, etc. In a sample synthesized at 70°C, well-formed grape-like spheres with worm-like pores were observed by SEM and TEM. The average pore size is ca. 1.87nm and the specific surface area of the spheres is 865m2/g. The hydrogen storage capacity of the sample Pd/SMS-70-C, prepared by supporting 5wt% palladium on SMS (synthesized at 70°C), is up to 2.56wt% at 1.2MPa hydrogen pressure. [Copyright &y& Elsevier]