Search

Herein, the vertical thin nickel–iron layered double hydroxide nanosheets grown on the hills-like nickel framework (NiFe LDH/Ni@NF) are employed for the oxygen evolution reaction (OER), securing at the low overpotentials of 197 and 270 mV to obtain the current densities of 20 and 100 mA cm−2, respectively, with a Tafel slope of 73.34 mV dec−1. The electrodeposited nickel film induces the NiFe LDH nanosheets grow vertically and thinly. As well, the nickel abundant interfaces and inner space makes this catalyst effective for OER. It was further served as the OER electrode in a water splitting system coupled the Pt/C cathode, and a cell voltage was at 1.52 and 1.67 V to achieve the current density of 10 mA cm−2 and 50 mA cm−2. In addition, the water electrolyzer can suffer a long time of 24 h at 50 mA cm−2, showing the feasibility in a practical unbiased alkaline water splitting system. • The vertical thin Ni 4 Fe 1 LDH-16h was prepared on the hills-like nickel framework. • The crosslinked nanosheets can offer amounts of active sites for OER. • It achieves a low overpotential of 197 mV to drive 20 mA cm−2 for OER. • The assembled electrolyzer exhibits enhanced performance. [ABSTRACT FROM AUTHOR]

Porous Ni 2 P nanoflower supported on nickel foam (Ni 2 P@Ni foam) electrodes are synthesized via a simple hydrothermal growth strategy accompanied with further phosphating treatment. The prepared electrodes are characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX) and transmission electron microscopy (TEM). Electro-catalytic performances towards urea electro-oxidation are tested by cyclic voltammetry (CV), chronoamperometry (CA) coupled with electrochemical impedance spectroscopy (EIS). By phosphating Ni(OH) 2 precursor, the final obtained Ni 2 P@Ni foam electrode presents a porous Ni 2 P nanoflower structure within abundant porosity, and so exposes a large amount of electro-catalytic active sites and electronic transmission channels to accelerate the interfacial reaction. Compared with Ni(OH) 2 @Ni foam precursor, the Ni 2 P@Ni foam catalyst exhibits more excellent electro-catalytic activity as well as lower onset oxidation potential. Remarkably, the Ni 2 P@Ni foam catalyst reaches a peak current density of 750 mA cm −2 with an onset oxidation potential of 0.24 V (vs. Ag/AgCl) accompanied by an excellent stability in 0.60 M urea with 5.00 M KOH solutions. Benefiting from the unique porous nanosheet structure, the as-synthesized Ni 2 P@Ni foam catalyst performs a highly enhanced catalytic behavior for alkaline urea electro-oxidation, indicating that the material can be hopefully applied in direct urea fuel cells. [ABSTRACT FROM AUTHOR]

Thorn-like Ni@TiC NAs and flake-like Co@TiC NAs electrodes without any conductive agent and binder are simply fabricated by the potentiostatic electrodeposition of Ni and Co catalysts on the TiC nanowire arrays (NAs). The electrocatalytic activity of H 2 O 2 oxidation on the Ni@TiC NAs electrodes is better than that on the Co@TiC NAs electrodes. The Ni@TiC NAs electrodes demonstrate a rough surface and have many nano-needles on the rod edges, which assures the high utilized efficiency of Ni catalysts. These particular three-dimensional structures may be very suitable for H 2 O 2 electrooxidation. The anodic current of Ni@TiC NAs anode reaches 0.32 A cm −2 at 0.3 V in 1.0 M H 2 O 2 + 4 M KOH solution. The DPFCs employing Ni@TiC NAs anodes display the peak power density of 30.2 mW cm −2 and open circuit voltage of 0.90 V at 85.1 mA cm −2 with desirable cell stability at 10 mL min −1 flow rate and 20 °C, which is much higher than those previously reported. [ABSTRACT FROM AUTHOR]