Search

Abstract: The growth of CuO nanosheet arrays on Cu foil was demonstrated. The morphology and structure of the CuO were examined by scanning electron microscopy and X-ray diffraction spectroscopy. The catalytic performance of the obtained CuO/Cu electrode for hydrogen peroxide electroreduction in 3.0moldm−3 KOH was evaluated by means of cyclic voltammetry and chronoamperometry. The CuO/Cu electrode shows an onset potential for H2O2 electroreduction comparable to Co3O4 nanowire arrays grown on Ni foam and around 100mV more negative than precious metal catalysts, such as Pt and Pd, demonstrating its good catalytic activity for H2O2 electroreduction. The stabilized mass current density for H2O2 electroreduction on the CuO/Cu electrode at −0.3V reached about 57% of that on Co3O4 nanowire arrays grown on nickel foam. Compared to conventional fuel cell electrodes fabricated by mixing active materials with conducting agents and polymer binders, this electrode of CuO nanosheet arrays directly grown on Cu has superior mass transport property, which combining with its low-cost and facile preparation, make it a promising electrode for fuel cell using H2O2 as the oxidant. [Copyright &y& Elsevier]

Abstract: Au/Ni-foam electrodes with three dimensional network structures are prepared by simple spontaneous deposition of nano-sized Au particles onto nickel foam surface in an aqueous solution of AuCl3. Their morphology and catalytic performance for NaBH4 electrooxidation and H2O2 electroreduction in NaOH solution are investigated. Au particles with diameters smaller than 100nm are uniformly deposited on the whole surface of all skeletons of the nickel foam substrate. The onset potential for NaBH4 electrooxidation and H2O2 electroreduction is about −1.2V and −0.1V, respectively. A direct liquid feed alkaline NaBH4–H2O2 fuel cell is constructed using Au/Ni-foam electrode as both the anode and the cathode. The effects of the concentration of NaBH4 and H2O2 and operation temperature on the fuel cell performance are investigated. The fuel cell exhibits an open circuit voltage of about 1.07V and a peak power density of 75mWcm−2 at a current density of 150mAcm−2 and a cell voltage of 0.5V operating on 0.2moldm−3 NaBH4 and 0.5moldm−3 H2O2 at 40°C. [Copyright &y& Elsevier]

Direct peroxide-peroxide fuel cell (DPPFC) employing with H 2 O 2 both as the fuel and oxidant is an attractive fuel cell due to its no intermediates, easy handling, low toxicity and expense. However, the major gap of DPPFC is the cathode performance as a result of the slow reaction kinetics of H 2 O 2 electro-reduction and thus the target issue is to design cathode catalysts with high performance and low cost. Herein, different with using noble metal of state-of-the-art, we have successfully synthesized ultra-fine Ni Fe ferrocyanide (NiFeHCF) nanoparticles (the mean particles size is 2.5 nm) through a co-precipitation method, which is used as the cathode catalyst towards H 2 O 2 reduction in acidic medium. The current density of H 2 O 2 reduction on the resultant NiFeHCF electrode after the 1800 s test period at −0.1, 0 and 0.1 V are 121, 93 and 76 mA cm 2 , respectively. Meanwhile, a single two-compartment DPPFC cell with NiFeHCF nanoparticles as the cathode and Ni/Ni foam as the anode is assembled and displayed a stable OCP of 1.09 V and a peak power density of 36 mW cm −2 at 20 °C, which is much higher than that of a DPPFC employed with Pd nano-catalyst as cathode. [ABSTRACT FROM AUTHOR]

Thorn-like Ni@TiC NAs and flake-like Co@TiC NAs electrodes without any conductive agent and binder are simply fabricated by the potentiostatic electrodeposition of Ni and Co catalysts on the TiC nanowire arrays (NAs). The electrocatalytic activity of H 2 O 2 oxidation on the Ni@TiC NAs electrodes is better than that on the Co@TiC NAs electrodes. The Ni@TiC NAs electrodes demonstrate a rough surface and have many nano-needles on the rod edges, which assures the high utilized efficiency of Ni catalysts. These particular three-dimensional structures may be very suitable for H 2 O 2 electrooxidation. The anodic current of Ni@TiC NAs anode reaches 0.32 A cm −2 at 0.3 V in 1.0 M H 2 O 2 + 4 M KOH solution. The DPFCs employing Ni@TiC NAs anodes display the peak power density of 30.2 mW cm −2 and open circuit voltage of 0.90 V at 85.1 mA cm −2 with desirable cell stability at 10 mL min −1 flow rate and 20 °C, which is much higher than those previously reported. [ABSTRACT FROM AUTHOR]