Abstract At present, there is an urgent need for plentiful non-noble metal catalyst to substitute for valuableness platinum based metal catalyst in electrochemical water splitting. Here, we fabricated a three-demensional (3D) Ni Co NiCo 2 O 4 nanosheets electrocatalyst that directly grew on Ni foam firstly and then were reduced in 0.1 mol dm−3 sodium borohydride solution. This electrode exhibited high activity in 1.0 mol dm−3 KOH solution with an onset potential of ∼40 mV and a tafel slope of 77 mV dec−1. Furthermore, the Ni Co NiCo 2 O 4 /NF electrode showed a splendid durability during long-playing electrochemical test. Our work may provide an inexpensive, easy-to-obtain and excellent catalyst candidate for future electrolytic water research and industry studies that may involve hydrogen applications in the future. Highlights • The Ni Co NiCo 2 O 4 /NF is an inexpensive, easy-to-obtain and excellent electrode. • When the current density up to 10 mA cm−2 requires an overpotential 125 mV. • Metallic Ni and Co core enhance the electrode activity. [ABSTRACT FROM AUTHOR]

Thorn-like Ni@TiC NAs and flake-like Co@TiC NAs electrodes without any conductive agent and binder are simply fabricated by the potentiostatic electrodeposition of Ni and Co catalysts on the TiC nanowire arrays (NAs). The electrocatalytic activity of H 2 O 2 oxidation on the Ni@TiC NAs electrodes is better than that on the Co@TiC NAs electrodes. The Ni@TiC NAs electrodes demonstrate a rough surface and have many nano-needles on the rod edges, which assures the high utilized efficiency of Ni catalysts. These particular three-dimensional structures may be very suitable for H 2 O 2 electrooxidation. The anodic current of Ni@TiC NAs anode reaches 0.32 A cm −2 at 0.3 V in 1.0 M H 2 O 2 + 4 M KOH solution. The DPFCs employing Ni@TiC NAs anodes display the peak power density of 30.2 mW cm −2 and open circuit voltage of 0.90 V at 85.1 mA cm −2 with desirable cell stability at 10 mL min −1 flow rate and 20 °C, which is much higher than those previously reported. [ABSTRACT FROM AUTHOR]