Search

Lignin can be used as a sustainable alternative to bisphenol A (BPA) to prepared lignin-based epoxy resins. Lignin effects including molecular weight, phenolic content, G/S unit ratio and flexible/rigid linkage ratio on epoxy synthesis and performance were summarized comprehensively. The incorporation of lignin with a higher molecular weight would lead to the higher rigidity of epoxy crosslinking network. Higher contents of ether bonds in lignin would provide higher structural flexibility of lignin incorporated epoxy thermosets. Lignin with higher contents of phenolic hydroxyls was more beneficial for improving the reactivity of its epoxy products after glycidylation. Due to the excellent charring capacity of lignin, higher contents of residue char can be produced at higher additions of lignin at high temperatures, while the loss of crosslinking density caused by the increasing lignin addition (especially for the macromolecular lignin) would deteriorate the thermal stability of their thermosets. Several applications of lignin-based epoxy resins were also mentioned based on their mechanical, thermal and chemical properties, such as coatings (with anticorrosion and UV-blocking), adhesives (with highly crosslinking network, excellent mechanical, and thermal properties) and flame retardants (with high charring capability). [Display omitted] [ABSTRACT FROM AUTHOR]

Obtaining lignin-based graphite-like microcrystallites at a relatively low carbonization temperature is still very challenging. In this work, we report a new method based on condensed structures, for regulating graphite-like microcrystalline structures via the incorporation of 4,4′-diphenylmethane diisocyanate (MDI) into the main structure of lignin. The effects of MDI on the thermal properties of lignin and the graphite-like microcrystalline structure of lignin-based ultrafine carbon fibers were extensively studied and investigated. The incorporation of MDI decreased the thermal stability of lignin, increased the carbon yield and enhanced the formation of graphite-like microcrystallites, which are beneficial for reducing energy consumption during the preparation of lignin-based carbon fibers. The modified lignin-based ultrafine carbon fibers (M-LCFs) demonstrated satisfactory electrochemical performance, including high specific capacitance, low charge transfer resistance, and good cycle performance. The M-LCFs-3/2 electrode had a specific capacitance of 241.3 F g−1 at a current density of 0.5 A g−1, and a residual ratio of 90.2 % after 2000 charge and discharge cycles. This study provides a new approach to control the graphite-like microcrystalline structure and electrochemical performance while also optimizing the temperature. • Lignin-based carbon fiber with graphite structure was prepared at a low temperature. • Condensed structure facilitate the formation of graphite-like structure. • MDI decreased the thermal stability of lignin and energy consumption of carbon fiber. • MDI-modified lignin shows fascinating application in supercapacitor. [ABSTRACT FROM AUTHOR]

Organic onium hydroxide aqueous solutions (OHAS) are demonstrated to be potential solvents for the dissolution of lignin and its epoxidation. A series of OHAS has been assessed in terms of the solubility of soda lignin (SL) and Klason lignin (KL), which are moderately and rarely soluble in NaOH aq. soln., respectively. Tetrabutylphosphonium hydroxide ([P 4444 ]OH) aqueous solution was found to exhibit a highest solubility, specifically 40 wt% of SL and 3.0 wt% of KL. The superior solubility of OHAS is comprehended to be due to weak interactions between OH anions and phosphonium cations, and hence OH anions interact effectively with lignin. Epoxidation of SL was achieved by simply adding epichlorohydrin to [P 4444 ]OH aq. dissolving SL. Films of epoxidized SL were prepared by thermal curing with the aid of a crosslinking agent, and the films were found to possess high thermal stability of >250 °C and excellent ductility. The thermal and mechanical properties were controllable by the concentration of [P 4444 ]Cl as an additive. [ABSTRACT FROM AUTHOR]