Biodegradable composites were prepared from polylactic acid (PLA) and bamboo charcoal (BC) by melt blending and hot pressing. The effects of BC addition on the mechanical properties, water absorption, DMA, TGA, DSC, and CONE of BC/PLA composites were investigated. The microscopic morphology of the composites was analyzed by SEM. The results showed that for BC addition of 40 wt%, the mechanical strength, thermal properties, and flame retardant properties of the composites were improved compared with those of PLA, with a 2.24 % increase in flexural strength and a 1535 % increase (500 °C) in TG mass retention rate. The crystallinity increased by 129.66 %, the peak loss factor decreased by 31.15 %, the time required for combustion was delayed by 168 s, the peak heat release rate decreased by 29.40 %, the carbon residue rate detected by cone calorimetry increased by 48.50 %, and the peak mass loss rate decreased by 48.82 %. The addition of BC enhanced the crystallization capacity of PLA, and improved the thermal properties and flame retardant properties of the prepared composites. The results showed that materials prepared with a BC content of 40 wt% exhibited the best overall performance., (Copyright © 2022 Elsevier B.V. All rights reserved.)

Applications for polylactic acid (PLA) are significantly impacted by its poor mechanical properties and lack of thermal stability. The goal of this work is to bridge the gap of poor compatibility among the components and enhance their interface interlocking capability to improve the toughness and thermal stability. Ultrafine bamboo charcoal (UFBC) was treated through deep eutectic solvent (DES) method to deposit sodium lignosulfonate (LS) on its surface. LS was used with PLA as a bio-coupling agent to create an eco-friendly PLA composite film with a wide range of characteristics. Benefiting from the penetration of PLA to the internal pores in UFBC, the resultant L-UFBC/PLA film has a good mechanical interlocking structure. Ls can increase the compatibility and strengthen the interface interlocking capability through DES method, which greatly improves the mechanical properties of the system. In comparison to pure PLA one, the elongation at break was 136.24 % greater, and the crystallinity (Xc) increased from 1.09 % to 3.33 %. Furthermore, the thermal stability of the system was also improved, and the residual at 600 °C rose by 4.83 %. These characteristics offer the prepared L-UFBC/PLA film a wide range of potential applications in the packaging, medical, agricultural, and other sectors. [ABSTRACT FROM AUTHOR]