1. Influence of LaMgAl11O19 On Solid Particle Impact Erosion Wear Behavior of 3 YSZ Ceramic at Elevated Temperatures.
- Author
-
Fang, Minghao, Min, Xin, Liu, Yan'gai, Liu, Fengjiao, Tang, Chao, Wang, Xiaojun, Wu, Xiaowen, and Huang, Zhaohui
- Subjects
MAGNESIUM alloys ,ALUMINUM oxide ,IMPACT (Mechanics) ,MECHANICAL properties of metals ,EFFECT of temperature on metals ,MECHANICAL wear - Abstract
To study the improvement in solid particle impact erosion wear resistances of 3 mol% yttria-stabilized zirconia (3YSZ) ceramic at elevated temperatures up to 1400°C, 2 wt% LaMgA1
11 O19 was added into 3YSZ to prepare LaMgA111 O19 -3YSZ ceramic for erosion resistance tests with angular corundum abrasive particles. The testing results show that the volume erosion rates of 3YSZ and LaMgA111 O19 -3YSZ ceramic were similar in the temperature range from room temperature to 600°C, then exhibited a sharp increase from 600°C to 1200°C, and dropped again at 1400°C. It was mainly caused by the change in material removal mechanisms from plastic deformation below 600°C to the interaction of transverse cracks in the temperature range from 600°C to 1400°C. The solid particle impact erosion wear properties of 3YSZ ceramic in the temperature range from 600°C to 1400°C were successfully improved by the addition 2 wt% LaMgA111 O19 platelets. Comparing with the volume erosion rate of pure 3YSZ ceramic (0.687 mm3 /g) at 1200°C, the value of LaMgA111 O19 -3YSZ ceramic (0.551 mm3 /g) has been decreased by 20%. [ABSTRACT FROM AUTHOR]- Published