The keyhole behaviors were observed directly by laser welding experiment with quartz glass. Based on Fresnel absorption of laser beam and multi-reflection combined with volume of fluid (VOF) method, a three-dimensional mathematical model was established to study the role of welding speed on keyhole behaviors and keyhole-induced porosity formation in laser welding of aluminum alloy. The keyhole behaviors and weld pool fluid flow were discussed, and the result shows that, although the welding speed varies, the mechanism of keyhole collapse was similar. However, the keyhole stability at higher welding speed was improved due to reduced weld depth fluctuations, spatter number, keyhole depth to width ratio, and keyhole collapse frequency. Furthermore, the improved keyhole stability impeded the keyhole collapse, and the lower weld depth and solidification rate facilitated bubble escaping from the weld pool easily, which are the main factors for suppression of porosity at higher welding speed. [ABSTRACT FROM AUTHOR]

Hybrid laser-MIG (metal inert gas) welding has not been extensively applied in welding of aluminium alloy with thickness more than 10 mm because of the existence of weld defects and low joint strength. In this study, an original hybrid laser-MIG welding plus MIG welding process was developed. Double-sided hybrid laser-MIG welding method was designed and applied to the welding of 30-mm-thick Al 5083 alloy. The process was then optimized by overlaying a MIG welding upon the weld. Analysis on the weld revealed that the overlaid MIG welding played multiple roles, including making up the bead formations, eliminating the keyhole-induced porosities as well as refining grains. Along the longitudinal direction of the weld, the grains became finer from two fringes to the middle, and the mechanical properties improved accordingly. Compared with MIG welding, the hybrid laser-MIG welding plus MIG welding process showed overwhelming superiorities over the MIG welding, which will be promising in industrial applications. [ABSTRACT FROM AUTHOR]