In this paper, a disk laser welding was developed to join 3-mm thin-Sect. 30Cr3 ultra-high-strength steel which was widely used in aerospace. The microstructure and mechanical properties of welded joint were investigated in detail. The results indicated that the recommended laser linear energy range were between 150 and 165 J/mm to guarantee that the melting width was up to 1 mm as well as less oxidation, spatter, and depression on the weld. Meanwhile, for the as-welded (AW) condition, the base metal (BM) consisted of ferrite matrix with distributing small spherical carbides, also known as spherical pearlite. While, the fine grained region, coarse grained region, and weld metal were all composed of martensite. However, the partially transformed region mainly consisted martensite with a little of spherical pearlite. Meanwhile, the average grain sizes of weld metal, HAZ, and base metal were 1.3 μm, 1.5 μm, and 1.8 μm, respectively. However, for the post-weld heat treatment (PWHT) condition, the whole welded joint was all composed of tempered martensite, and the average grain size of welded joint was about 1.7 μm. The tensile strength of the welded joint was higher than that of the base metal both in the AW and PWHT condition as all the fracture with shrinkage occurred in the BM of the specimens. Additionally, the average yield strength of the AW and PWHT are about 600 MPa and 1700 MPa, respectively. [ABSTRACT FROM AUTHOR]

Additive manufacturing (AM) has various independent parameters that affect the mechanical properties and quality of the produced parts that are not linearly the function of each other. Process parameters in metal AM are very hard to control, analyse and optimise because they affect each other even though they can be independently changed. Changing process parameters in a wide range is not possible due to the formation of problems such as cracks, balling, unmelted powders, porosity and distortion. In this paper, a numerical model to predict the value of tensile strength of selective laser melting (SLM) Ti-6Al-4V parts and analyse the effect of process parameters on the results has been proposed. Taguchi L25 Design of Experiment (DOE) across 125 samples to create a comprehensive and general overview of influential parameters on the build process was investigated. Specifically, parameters included laser power, scan speed, hatch spacing, laser pattern angle and heat treatment (HT). To evaluate and analyse the build process according to established statistical variances, a minimum of five samples based on ASTM standard (for tensile test) were prepared. Heat treatment was added to the DOE to analyse the combined process and post-process effects. Results were compared (cross-validated) against existing values found in the literature and were found to effectively predict and explain the behaviour of tensile strength when changing process parameters. [ABSTRACT FROM AUTHOR]