Search

Purpose: The evaluation of the haptics of water taps and wear-related changes during usage usually involves time- and cost-intensive testing. The purpose of this paper is to abstract the tribo-system between technical ceramic disks of water tap mixer cartridges to the model level and study the tribological behavior. Design/methodology/approach: The friction and wear behavior was studied by means of an alumina ball-on-original alumina disk setup at different temperatures as well as under dry conditions and under lubrication by different greases. Thereby, the frictional behavior was measured in situ, and the wear losses were analyzed by means of laser scanning microscopy. Findings: It was shown that friction and wear can behave in a contrasting way, whereby one grease might lead to low friction, that is, an easy-going movability of the water tap, but to increased wear losses. The latter, in turn, is an indicator for the usability and service life, which cannot be explained from friction alone. Thereby, the viscosity of the base oil, the grease consistency and additives were identified as relevant grease formulation parameters to allow for fluid film (re-)formation and removal of wear particles. Originality/value: To the authors' best knowledge, this is the first approach to systematically analyze the friction and wear behavior of technical ceramic disks of water tap mixer cartridges in dependency on the temperature as well as the used lubricating grease. This approach is relevant for developing screening test strategies as well as for the selection of lubricants for water tap applications. Peer review: The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-11-2022-0334/ [ABSTRACT FROM AUTHOR]

Purpose: The curved and tribologically highly stressed surfaces of bearing components pose a major challenge for steel alloys or tribological resistant coatings like tetrahedral amorphous carbon (ta-C) coatings which in particular have an increased risk of delamination due to the significantly increased residual stresses. A possibility to prevent coating failure is the use of dopants while maintaining or even increasing tribological properties. This study aims to compare the tribological behavior of several doped diamond-like-carbon coatings with an undoped ta-C coating under varying slip conditions and Hertzian pressure up to 1800 MPa. Design/methodology/approach: For this purpose, the tribological behavior was studied using of a ball-on-disc tribometer and a two-disc test rig under mixed/boundary conditions. The tests were conducted with coated specimens against uncoated 100Cr6 steel. Additionally, the influence of lubrication additives was studied due to the use of two fully formulated PAO-based oils, one without and one with molybdenum containing additives. The friction was measured in situ, and the wear was analyzed trough laser scanning microscopy and tactile measurement. Findings: It was shown that the use of doped ta-C coatings exhibited a tendency for a more favorable tribological behavior compared to undoped ta-C coatings, with no general dependence on the lubricants used. The use of the most suitable coatings reduced the wear of the steel counter-body considerably. Originality/value: To the best of the authors' knowledge, this is the first approach of testing the tribological behavior of these doped ta-C coatings, developed for friction efficiency, in dependency on lubrication additives under the given load collective. The approach is relevant to determine whether the friction reduction and the wear inhibition of these coatings are suitable for higher contact pressures and load cycles. Peer review: The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-11-2022-0336/ [ABSTRACT FROM AUTHOR]