Objectives: This study assessed the effects of blue and Er:YAG lasers, fluoride varnish, and their combination on microhardness, and calcium and phosphorus content of demineralized enamel. Materials and Methods: The primary Vickers microhardness of 28 third molars was measured and their enamel calcium and phosphorous content was quantified by energy-dispersive X-ray spectroscopy. They were then randomly assigned to five groups of 5% sodium fluoride (NaF) varnish, 445nm blue laser, Er:YAG laser, 5% NaF + 445nm blue laser, and 5% NaF + Er:YAG laser. The teeth then underwent pH-cycling to induce caries-like lesions. The surface microhardness of the teeth and the calcium and phosphorous content of demineralized enamel were measured again. Data were analyzed by one-way ANOVA and Tukey’s test (alpha=0.05). Results: NaF, NaF-diode laser, and NaF-Er:YAG laser groups experienced a significant increase in microhardness of demineralized enamel close to the baseline value (P

Objectives: The aim of this study was to assess the microtensile bond strength of three universal adhesives to dentin and enamel. Materials and Methods: Sixty extracted human third molar teeth were chosen and divided into six groups regarding the adhesive (G-Premio Bond, Clearfil S3 Bond or Single Bond) and tooth surface. All the applied bonding agents were universal adhesives. The teeth were polished and the adhesives were applied; then the teeth were restored with composite resin. The samples were mounted in acrylic resin and sectioned. The specimens were subjected to a universal testing machine and the microtensile bond strength was measured. The failure mode of each specimen was determined under a stereomicroscope. Data were analyzed using two-way ANOVA (α=0.05). Results: The microtensile bond strength of G-Premio Bond to enamel and dentin was 11.79±8.27 and 17.55±9.47 MPa, respectively which was not significantly different from the values in Single Bond group (15.59±10.66 and 17.19±10.09 MPa to enamel and dentin, respectively; P>0.05). However, the values for Clearfil S3 Bond were 7.11±4.23 and 7.88±8.83 MPa to enamel and dentin, respectively, which were significantly lower than the values for G-Premio Bond (P