Search

WO3 nanorods and GO (at 1 wt% loading) doped WO3 were synthesized using a template free deposition-hydrothermal route and thoroughly characterized by various techniques including XRD, FTIR, Raman, TEM-SAED, PL, UV-Vis, XPS, and N2 adsorption. The nano-materials performance was investigated toward photocatalytic degradation of methylene blue dye (20 ppm) under visible light illumination (160 W, λ> 420) and gas sensing ability for ammonia gas (10–100 ppm) at 200°C. HRTEM investigation of the 1%GO.WO3 composite revealed WO3 nanorods of a major d-spacing value of 0.16 nm indexed to the crystal plane (221). That relevant plane was absent in pure WO3 establishing the intercalation with GO. The MB degradation activity was considerably enhanced over the 1%GO.WO3 catalyst with a rate constant of 0.0154 min−1 exceeding that of WO3 by 15 times. The reaction mechanism was justified dependent on electrons, holes and •OH reactive species as determined via scavenger examination tests and characterization techniques. The drop in both band gap (2.49 eV) and PL intensity was the main reason responsible for enhancing the photo-degradation activity of the 1%GO.WO3 catalyst. The later catalyst initiated the two electron O2 reduction forming H2O2, that contributed in the photoactivity improvement via forming •OH moieties. The hexagonal structure of 1%GO.WO3 showed a better gas sensing performance for ammonia gas at 100 ppm (Ra-Rg/Rg = 17.6) exceeding that of pure WO3 nanorods (1.27). The superiority of the gas-sensing property of the 1%GO.WO3 catalyst was mainly ascribed to the high dispersity of GO onto WO3 surfaces by which different carbon species served as mediators to hinder the recombination rate of photo-generated electron-hole pairs and therefore facilitated the electron transition. The dominancy of the lattice plane (221) in 1%GO.WO3 formed between GO and WO3 improved the electron transport in the gas-sensing process.

A simple hydrothermal route assisted by a triblock copolymer was used to synthesize Ag2O/Ag nanoparticles on a robotic support consists of functionalized MWCNTs and graphene composite (Ag2O/Ag/CNT-graphene). The composites together with the individual analog of Ag/CNT and Ag/graphene were characterized by means of XRD, TEM-SAED, N2 sorptiometry, Raman, FTIR, UV-Vis, and photoluminescence spectroscopy. These nanomaterials were then tested for the catalytic reduction of 4-nitrophenol (4-NP) to the technologically beneficial 4-aminophenol (4-AP). The Ag2O@Ag@CNT-graphene composite calcined at 400°C has shown fascinating reduction performances for 4-NP either in the dark (k = 0.014 s−1) or under visible light illumination (k = 0.039 s−1) in the presence of 5 mM NaBH4 compared to Ag/CNT (0.0112 s−1) and Ag/graphene (0.010 s−1) catalysts. This was chiefly because Ag2O@Ag@CNT-graphene comprises the highest pore volume (0.49 cm3/g) and involves three types of pores in the margin from 1.8 to 4.0 nm in front of only one modal type of pores for the rest of the catalysts and thus maximizes the adsorptive capacity of the reactants (4-NP and NaBH4). Moreover, the former composite exhibits the highest concentration of the Ag2O component as established by numerous techniques in addition to the cyclic voltammetry, proposing it's facile reaction with 4-NP along with the simultaneous transfer of surface hydrogen and electrons from NaBH4 ions to produce 4-AP. The promotion of the p-n junction evaluated using the Mott-schottky equation on Ag2O@Ag@CNT-graphene assisted by charges separation and surface plasmon resonance bands of Ag and Ag2O are found to be advantageous for 4-NP reduction. The latter composite delivers a specific capacitance of 355 F g−1 at 1.0 A g−1 exceeding those of Ag/CNT (230 F g−1) and Ag/graphene (185 F g−1). The EIS study establishes the high electronic conductivity of the metallic Ag and Ag2O moieties, low internal resistance of CNT-graphene as well as the marked ionic transfer facilitated by the composite porous nature.