Search

Dibutyl phosphate-bound natural rubber (DBNR) was prepared by reacting epoxidized natural rubber with 20 mol% (ENR-20) with dibutyl phosphate in a latex medium. Fourier transform infrared spectroscopy (FTIR) was used to confirm the molecular structures of ENR-20 and DBNR and to quantify the epoxide contents. The shear flows and thermal properties of DBNR were then characterized and compared with ENR-20 and natural rubber (NR). The DBNR exhibited the lowest viscosity curves, but it depicted the highest glass transition temperature (Tg) and residue from thermogravimetric evaluation, indicating higher thermal resistance. Subsequently, different NR/DBNR blend ratios were compounded, with and without flame resistance additives, compared with unmodified NR and chloroprene rubber (CR) compounds. We found that all natural rubber compounds exhibited reversion behavior due to the breakage of newly formed sulfidic bonds. However, chloroprene rubber showed marching cured curves, as evidenced by the increasing torque with prolonged testing time. Additionally, antimony trioxide retarded the curing reaction of NR, while tris(2-ethylhexyl) phosphate accelerated it. Therefore, the combination of these additives synergists with the intrinsic flame retardant properties of DBNR. The study revealed that the burning rate of NR/DBNR blends, exhibited very high flame resistance capability compared to gum NR and NR compounded with flame resistance additives. [ABSTRACT FROM AUTHOR]

A promising process to design non-isocyanate polyurethane (NIPU) foams has been developed. The transurethane polycondensation reaction between fatty biscarbamates, fatty diols, and diamines was used to synthesize a biobased aminotelechelic NIPU oligomer. The prepared oligomer (hard phase) was mixed with an amino-telechelic polydimethylsiloxane (PDMS, soft phase) and then reacted with a biosourced tri-epoxide molecule as crosslinking agent, in the presence of water/ethanol mixtures as physical blowing agents. The crosslinking reaction was followed by Fourier transform infrared spectroscopy (FTIR) and rheometry. The foams can be obtained in less than 2 hours at 95 °C. The prepared foams exhibited cell diameters ranging from 130 to 3090 μm, as well as densities ranging from 55 to 950 kg/m3. Their thermal stability thresholds were above 300 °C. They displayed glass transition temperature values ranging from –20 to –18 °C, and low values of the Young modulus ranging from 2.0·103 to 5.7·103 Pa. The hysteresis loss, the recovery time, and the firmness of these foams were dependent on the PDMS content and/or the morphological parameters. [ABSTRACT FROM AUTHOR]

Based on atomic force microscopy (AFM) and Fourier transform infrared spectroscopy (FTIR) analysis of the rubber-filler gel (wetting concept) the kinetics of selective wetting of carbon nanotubes (CNTs) in ternary styrene butadiene rubber (SBR)/butadiene rubber (BR)/natural rubber (NR) blends was qualitatively and quantitatively characterized. Almost all CNTs are found to be wetted by the non-polar NR but not by the other non-polar rubber like BR or weakly polar SBR. It was proposed that phospholipids, which are linked to the "-terminal of NR can interact with the CNT surface through cation-# interactions forming strong bonding between NR and CNTs. Using the corrected surface tension value of NR, which involves the effect of phospholipids found in our previous work the selective wetting of CNTs in ternary rubber blends can be well predicted using the Z-model for a thermodynamic equilibrium state. By replacing the non-polar BR by a polar rubber like nitrile butadiene rubber (NBR) as a blend component CNTs are wetted by NBR slightly more than by NR thanks to the strong interaction between CNTs and nitrile groups of NBR. SBR remains unbound to CNTs in both blends. [ABSTRACT FROM AUTHOR]