• High cyclic tensile stress is the reason for the RCF damages in LPQ prepared hardened spots. • LPQT can prepare discrete hardened spots surrounded by transitional zone. • The transitional zone helps to alleviate the RCF damages in the hardened spot by decreasing the cyclic tensile stress. • RCF and wear resistances of the LPQT treated rail steel can be balanced by decreasing the transitional zone's thickness. Surface layer with heterogeneous microstructures (SLHM), characterized by hardened spots discretely embedded in a soft substrate, can be prepared by laminar plasma quenching (LPQ) to improve the wear resistance of the railway rail. However, severe rolling contact fatigue (RCF) cracks and spalling would occur in the hardened spots that only consist of quenched microstructure. This study analyzed the RCF damage mechanism of the LPQ prepared hardened spots by contact simulation. To improve the RCF resistance while maintaining the high wear resistance of the treated rail, a novel SLHM, whose discrete hardened spots are surrounded by transitional zone with the hardness lower than that of the quenched zone but higher than that of the substrate, was proposed and prepared by laminar plasma quenching-tempering (LPQT). Then, twin-disc tests and contact simulations were conducted to investigate the wear and RCF resistances of the LPQT treated rail steel. Results showed that the cause of the severe RCF cracks and spalling at the entry side of the LPQ prepared hardened spots was that the cyclic tensile stress at the entry side was always higher than that at the exit side under the cyclic rolling contact loading. The high tensile stress at the entry side of the LPQ prepared hardened spots resulted from the elastic deformation induced by tensile plastic deformation of the neighboring substrate. When the thickness of the transitional zone was about 0.1 mm, the generation of severe RCF cracks and spalling was significantly inhibited in the LPQT prepared hardened spots because the transitional zone decreases the cyclic tensile stress at the entry side of the quenched zone. Besides, the wear loss of such LPQT treated rail steel was only increased by 18.1 % compared with that of the LPQ treated rail steel, indicating that the wear resistance of the LPQT treated rail steel was not significantly reduced. These findings are promising for designing the microstructure of the surface layer to obtain wear-resistant rail with high RCF resistance. [ABSTRACT FROM AUTHOR]

• Increasing turbine rotor sizes have made main bearing reliability a major concern in modern turbines. • Industry and academia have played critical roles in improving the performance and service life of turbine main bearings. • Scholarly contributions have predominantly focused on the fields of bearing geometry and profile optimization. • Tapered roller bearings have received the most research attention compare to spherical roller bearings. • The authors recommend increased exploration of evolutionary bearing geometry optimization techniques. The growing demand for renewable energy has made wind turbines increasingly large and complex. Demand for efficient main bearings optimized to endure dynamic and unpredictable stresses while allowing turbine motion rises even more. Over the years, rolling element bearings have advanced to meet this demand, driven by innovations from industry and academia. This study examined industry-related and academic contributions to the advancement of wind turbine main bearings. Spherical and tapered roller bearings are identified as the basic wind turbine rotor bearings. From the works reviewed, it was found that industry-related contributions on these bearings center on bearing configuration improvements, cage improvements, the development of improved coats, and the design of novel evolutionary variants of the bearings. The SKF was identified as having contributed more to the development of wind turbine rotor bearings with the patenting of two novel bearings: the CARB toroidal bearing and the Nautilus. Scholarly contributions have majored in bearing geometry and profile optimization. Tapered roller bearings were found to have received more research attention than spherical roller bearings. Also, few innovative studies on CARB toroidal bearing, asymmetrical spherical roller bearing, and the Nautilus have been reported. Exclusively theoretical analyses have been mostly used in performance optimizations of the bearings. Only in a few studies did experimental investigations validate theoretical findings, creating potential avenues for experimental studies. Insights from the review indicate that tapered roller bearings or plain bearings could be viable substitute for spherical main shaft bearings, considering their persistent reliability challenges. The authors recommend more exploration of evolutionary bearing optimization techniques, more investigations on bearing lubricants, housing material, cage material, and coating material designs, and increased industry-academic engagement to pave the way for more main bearing innovation. [ABSTRACT FROM AUTHOR]

• Verified frog crack growth model combines impact simulation and fracture analysis. • Crack location and angle are more influential than train speed and axle load. • Observed accelerated growth of transverse cracks near the frog nose. • Proposed inspection strategy based on crack type, cumulative tonnage, and headway. Fatigue cracking is one of the notable failure mechanisms of railway turnout frogs due to high contact forces induced by the wheel-rail impact. However, the treatments specific to the frogs of cast high manganese steel to prevent sudden failure are rarely provided and are independent of the crack conditions, which can significantly affect the fatigue crack growth rate. To address this shortcoming, the fatigue crack growth in a cast high manganese steel frog is computationally investigated with varied wheel and crack conditions. The dynamic wheel-frog impact is first simulated to obtain the distribution of contact pressure imposed on the frog, and the propagation of the fatigue crack is then predicted using the finite element formulation in fracture mechanics. The simulation results show that the train speed and axle load can change the maximum contact stress. Nevertheless, when representing the growth rate in terms of the cumulative passing axle load, the effect of axle load and train speed on the crack growth is minimal and moderate, respectively. In contrast, the initial crack conditions, including the location and angle, have an overweighted influence. As a result, an inspection scheduling strategy for identified cracks with different conditions is proposed to consider both safety and operational efficiency. [ABSTRACT FROM AUTHOR]

• Three dynamic indicators for predicting plastic flow in railway systems based on the mechanics of wheel-rail contact, Tresca's yielding criterion and shakedown theory. • A dynamic method that is simple to model and fast to compute for predicting plastic flow in railway systems. • Key parameters affecting plastic flow and rolling contact fatigue. • A dynamic approach for the impact of plastic flow on rolling contact fatigue damage. • Effect of different degrees of plastic flow on rolling contact fatigue. To analyze the plastic flow of wheels and its impact on rolling contact fatigue (RCF), this article proposes a multibody dynamics approach that is simple to model and fast to compute, based on the mechanics of wheel-rail contact and Tresca yield criterion. This method is used to study the plastic flow of the wheels and is validated by comparing it with plastic flow analysis based on the shakedown theory. The study shows that the dynamics indicators of maximum shear stress, adhesion saturation and stress ratio effectively reflect the plastic deformation of the wheel. Additionally, increasing wheel speed and curve radius, and decreasing wheel-rail friction coefficient, can effectively reduce the area and severity of plastic deformation in the wheel. Ignoring the impact of temperature effects on RCF, it is found that the more severe the plastic flow, the greater the likelihood of RCF. That is, alleviating the plastic flow of the wheel can reduce RCF damage in wheels. This approach to managing the health of wheels provides a comprehensive understanding of the interplay between operational parameters and the mechanical behavior of wheel materials, guiding maintenance strategies and operational decisions to enhance safety and extend the lifespan of railway components. [ABSTRACT FROM AUTHOR]

• The hardness of the soft zone is much lower relative to the hardened surface of the raceway. • A hierarchical finite element modeling method of the main bearing is proposed. • The principle of selecting the optimum hardened depth is given. • The effect of the soft zone on the contact characteristics and fatigue life of the raceway is investigated. • This analyzing method can quickly and efficiently clarify the contact state in the soft zone during the rolling process. A hierarchical finite element modeling method is proposed to study the problem of fatigue spalling easily due to low hardness in the soft zone for the main bearing of a tunnel boring machine. Quasi-static analyses of the main bearing are performed based on the global symmetric model and verified by relative displacement tests of the rings. The invariant contact pressure is replaced by the rolling contact of the rollers in the local sub-model. The contact load is used as an input to solve the stress field, and then the effects of soft zone and hardened depth on the contact characteristics and fatigue lifetime of the sub-model are investigated. The results show there are stress peaks at the junction of the hardened and soft zones. The effect of hardened depth on the stress distribution and fatigue lifetime is relatively small. However, the optimum hardened depth is influenced by the contact load and the permissible stress of the material. The minimum lifetime of the raceway during rolling occurs in the soft zone. This paper achieves a fast and effective rolling contact fatigue analysis of the main bearing, which provides a theoretical basis for optimizing the main bearing design. [ABSTRACT FROM AUTHOR]

• A 3D FE model of wheelset-turnout-sleeper structure is established. • The ratcheting effect of turnout material is simulated. • A mixed implicit-explicit FE method is used to simulate the wheelset passing through the turnout. • The transient contact behavior of high-speed turnouts under cyclic loading is investigated. • The evolution of ratcheting strain of rail under different numbers of cycles and crossing speeds is discussed. The present work introduces a three-dimensional finite element model for the wheel-turnout-sleeper system, incorporating a cyclic constitutive model that accurately captures the nonlinear hardening behavior of rail steel under cyclic loadings. At the same time, a mixed implicit-explicit finite element method is employed to investigate the transient rolling contact behavior of wheel-turnout. Through dynamic analysis, the transient rolling contact status of the wheel-turnout, stress and strain responses of the turnout, and wheel-rail forces are investigated under varying crossing speeds and number of cycles. It is found that during the wheelset crossing, the contact stress remains relatively stable on the stock rail, and multi-point contact occurs at the wing rail and long point rail, and the contact stress on the surface of the long point rail is more significant. With an increase in crossing speed in the same cycle, there is a gradual rise in contact stress on the long point rail face. At the same crossing speed, with the increase in the number of cycles, the contact position between the wheelset and the long point rail gradually moves back, and the top width of the contact position gradually expands. Meanwhile, the fluctuation range of vertical displacement of the wheel center diminishes, and the wheel flange moves away from the long point rail. Additionally, a progressive accumulation of ratcheting strain is observed on the rail, and the ratcheting strain on the long point rail significantly exceeds that on the stock rail. The research results will help to provide a reference for the optimization and design of the critical cross-section profile of the long point rail and will have guiding significance for the maintenance and repair of turnouts. [ABSTRACT FROM AUTHOR]

• Typical factors affecting the wheel-rail dynamic response are comprehensively considered to reveal the short-term load characteristics of frog under complex conditions. Meanwhile, based on the ellipsoidal Gaussian extrapolation theory, long-term wheel-rail load characteristics are obtained. • Combined with the strain energy fatigue parameter theory, a prediction method for the fatigue life of nose rail under complex conditions based on load spectrum preparation was proposed. • The location between the 30 mm and 35 mm sections of the nose rail has the shortest rolling contact fatigue crack initiation life and should be focused on during damage inspection. The rail profile irregular variation and wheel-rail relationships complexity at the gap in the frog enhance the wheel-rail impact forces, frequently resulting in rolling fatigue damage under complex cyclic loads. Therefore, it is particularly important to study the transient rolling contact load characteristics of fixed frog and to compile load spectrum considering various complex conditions for analyzing the fatigue damage of frog and extending the service life of structure. In this paper, a 3D transient FE model of wheelset and fixed frog is established, revealing rolling contact behavior of wheel-rail in frog area from both macro and mesoscopic perspectives. In order to investigate long-term load characteristics of wheel and rail under complex service conditions, the changes of line conditions, load conditions, rail wear state and other influencing factors in actual operation are taken into account. Based on elliptic Gaussian kernel density theory, a method for compiling the load spectrum of fixed frog nose rail is proposed, and the FP method is used for fatigue crack initiation life prediction of nose rail in fixed frog. The results show that the force state is more severe when passing through the frog in straight reverse direction, and resonance is prone to occur in the third and fifth vertical bending modes of the frog, as well as the fourth and sixth vertical bending modes of the stock rail. The increase in factors such as speed, axle load, wheelset lateral displacement towards frog side and wing rail wear will exacerbate wheel-rail impact and shorten frog service life. Different factors have an impact on the overall amplitude, oscillation center range, and maximum frequency load of the wheel-rail force in the long-term load spectrum of the frog. The fatigue crack initiation area of nose rail is mainly in 30 mm–35 mm sections, which is consistent with the on-site flaw detection results, verifying the accuracy of the calculation method developed in this paper. [ABSTRACT FROM AUTHOR]

• Generation arc is subjected to triple acceleration of P - v - I. • Surface damage is a combination of mechanical and electrical damages after arcing. • Conductive AFM visually confirm the harmful effects of oxidation on conductivity. This study employs copper (Cu)-Cu rolling pairs to investigate the failure characteristics and surface damage mechanism of current-carrying tribological contacts under various conditions (contact load P = 40–180 N, rotation speed v = 4–600 rpm, and current I = 0–2.5 A). Based on synchronous current curves and video observations, the severe current fluctuations caused by the electric arc can be considered a criterion for the failure of rolling electrical contacts. Surface damage assessment through scanning electron microscopy, X-ray photoelectron spectroscopy, and atomic force microscopy (AFM), reveal ablation pits, oxidation, and roughening as primary manifestations of electrical damage. Post-rolling, the Cu on the surface was oxidized to copper (II) oxide. As the degree of oxidation increased, the conductive area in the AFM current map decreased significantly at a sample bias voltage of 1.5 V. Notably, arc generation was subjected to the triple acceleration of the contact load, rotation speed, and current. A back propagation (BP) neural network model was established to predict the running cycles before arc generation. Based on independent validation experiments under P = 120 N, I = 1.0 A, v = 400, and 600 rpm, the average prediction error of the proposed BP neural network model was 8.13 %. The results of this study facilitate the understanding of failure mechanism and predicting life cycles of rolling electrical contacts. [ABSTRACT FROM AUTHOR]

• Local quenching causes gradient distribution of microstructure and hardness in wheel. • The statistical correlation is: Hardness = −2.77 × Fraction of proeutectoid ferrite + 328.07. • Wear and rolling contact causes microstructure evolution of wheel. • Microstructure and hardness show a significant synergistic evolution law. High-speed train wheels have complex service environments during wheel–rail contact, and a comprehensive understanding of the microstructural inhomogeneity at the rim is critical for service safety assessment. The local quenching process in the vicinity of the rim will cause a difference in microstructure, directly affecting the service performance of the material. In this study, high-throughput characterization method based on material genome engineering was used, the methods for characterising and identifying the microstructure of wheel steel were developed using high-throughput scanning electron microscopy, and the accuracy and reproducibility of the methods were evaluated. A point-to-point research scheme for microstructure image and hardness data was designed based on the concept of statistical mapping characterization. The area fraction of the proeutectoid ferrite and micro-Vickers hardness distribution in a large size range of the key area of the rim and their internal correlation was obtained, these helped avoid statistical and representativeness limitations of traditional local selection analysis of microstructure and hardness. The results indicates that the area fraction of proeutectoid ferrite and micro-Vickers hardness showed a clear gradient distribution, and opposite distribution trend, with a high negative correlation. In addition, by observing the correlation between microstructure and hardness, and studying the evolution of microstructure, it was found that the microstructure and hardness of the rim near the tread demonstrated a significant synergistic evolution law under the influence of service, this was observed both statistically and microscopically. These findings enhanced the application prospects of the microstructure-performance statistical mapping method, and were beneficial in efficiently evaluating the service life and safety of key components. [ABSTRACT FROM AUTHOR]

• Based on the Hertzian contact distribution and creep-slip characteristics, the fatigue life of spinning bearings is predicted using the damage parameter theory of the critical plane method and the L-P theory. • The deviation rate between the finite element simulation and the theoretical calculation results is 6.61% • The rotation speed, friction coefficient and external load affect the fatigue life of spinning bearings, and better lubrication and excellent contact surface to extend the life. • A rotary bearing life experimental device verified the reliability of the theoretically calculated deviation rate is 3.86%. In order to ensure the longer working life of rolling guide bushing, this work proposed a fatigue life prediction model of spinning bearings based on the Hertzian contact distribution and creep-slip characteristic. The influence of different parameters on the fatigue life of spinning bearings was analyzed according to the damage parameter theory of the critical plane method and the L-P theory. Finally, the fatigue life prediction model of spinning bearings was verified through the finite element simulation combined with the experiments. The reliability results show that creep-slip characteristic and deformation lead to the contact zone stress of the spinning bearing firstly increases, decreases subsequently to zero and then increases to the peak value. The increase of rotational speed will make the fatigue life of the spinning bearing firstly increases and then decreases. With the increase of friction coefficient, its fatigue life will become smaller and smaller, and the increase of the external load will decrease its fatigue life. Meanwhile, the prediction error rate of the fatigue life prediction model proposed in this study is 4.60%, which is within the error tolerance. This study provides certain methods and ideas for fatigue life prediction of spinning bearings, and lays a theoretical foundation for the design of highly reliable spinning bearings. [ABSTRACT FROM AUTHOR]

• The model can account for the non-linear lifting of the flange groove and the effects of wheelset traverse and side roll. • The wheel tread and flange are alternately loaded with two wheel load transition areas in the frog area. • Wear in the flange bearing area is significantly higher than in the tread bearing area, with an increase of 59.7%. • RCF damage dominates in the wing rail and the two wheelload transition areas. • Reducing the speed to 15 km/h significantly improves the service performance of the fixed frog. The tram No. 3 turnout fixed frog uses a variation in the depth of the flange groove so that the wheel rolls over the frog area in a continuous flange bearing. This method of travelling over the turnout requires the wheel load to transition back and forth between the tread and the flange, resulting in wheel-rail impact, which in turn affects service life. In order to investigate its service characteristics, this paper has established a transient wheel-rail rolling contact finite element model for the No. 3 turnout fixed frog. The macroscopic dynamic response and microscopic wheel-rail contact solution as the tram passes through the turnout at different axle weights and speeds are analysed in detail, and the changing patterns of wear and fatigue damage are investigated. The research shows that rail wear is particularly severe in the wheel flange bearing area, approximately 1.6 times greater than in the tread bearing area. In addition, when tram speeds are reduced to 15 km/h, there is a significant reduction in wheel-rail impact and wear, thereby improving ride smoothness and safety. The results of this study are of great significance to the operation and maintenance of the No.3 fixed frog turnout. [ABSTRACT FROM AUTHOR]