Search

This paper investigates the influence of biochar, either as an individual component or in combination with high-temperature coke, on the slag foaming behavior. High-temperature coke serves as a reference. Three scenarios were considered to study the slag foaming behavior, each characterized by different slag chemical compositions. The results indicate that biochar can promote steady foaming for specific slags when the basicity (CaO/SiO2) falls within a range of 1.2 to 3.4. Experimental findings also reveal that stable foaming can be achieved when a mixture containing biochar and coke with a ratio of 1:1 is employed, with a minimum slag basicity of 1.0 and FeO content of 25 wt.%. The foaming range obtained using different FeO contents (15 wt.% to 40 wt.%) in the mixture surpasses the range observed with the individual application of coke or biochar. The X-ray diffraction (XRD) analysis showed that unrelated to the carbon source applied, the general pattern was that the phases larnite (Ca2SiO4) or dicalcium silicate were detected for slag foams with high basicity. Monticellite (CaMgSiO4) and magnesium iron oxide (Fe2MgO4) were predominant in slag foam samples, with the highest MgO content. The presence of monticellite and merwinite (Ca3MgSi2O8) occurred in samples with the lowest basicity. Eventually, the application of the mixture of coke and biochar showed the potential to obtain stable foaming across a wide range of slag compositions. [ABSTRACT FROM AUTHOR]

The influence of different carbon sources, including anthracite, calcined petroleum coke, three samples of high-temperature coke, biochar, and a mixture of 50 wt.% biochar and 50 wt.% coke, on slag foaming behavior was studied. The slag's composition was set to FeO-CaO-Al2O3-MgO-SiO2, and the temperature for slag foaming was 1600 °C. The effect of the carbon sources was evaluated using foaming characteristics (foam height, foam volume, relative foaming height, and gas fraction), X-ray diffraction (XRD), chemical analysis of the slag foams, Mossbauer spectroscopy, observation by scanning electron microscope (SEM), and energy-dispersive spectroscopy (EDS) mapping. Different foaming phenomena were found among conventional sources, biochar as a single source, and the mixture of coke and biochar. Biochar showed the most inferior foaming characteristics compared to the other studied carbon sources. Nevertheless, the slag foaming process was improved and showed slag foaming characteristics similar to results obtained using conventional carbon sources when the mixture of 50 wt.% coke and 50 wt.% biochar was used. The XRD analysis revealed a difference between the top and bottom of the slag foams. In almost all cases, a maghemite crystalline phase was detected at the top of the slag foams, indicating oxidation; metallic iron was found at the bottom. Furthermore, a difference in the slag foam (mixture of coke and biochar) was found in the presence of such crystalline phases as magnesium iron oxide (Fe2MgO4) and magnetite (Mg0.4Fe2.96O4). Notwithstanding the carbon source applied, a layer between the foam slag and the crucible wall was found in many samples. Based on the SEM/EDS and XRD results, it was assumed this layer consists of gehlenite (Ca2(Al(AlSi)O7) and two spinels: magnesium aluminate (MgAl2O4) and magnesium iron oxide (Fe2MgO4). [ABSTRACT FROM AUTHOR]