Search

This work presents the results of research on submicro- and nanocomposites with gradient properties, produced in a planned electrophoretic process. Epoxy-resin-based samples were filled with TiO2 particles of three different sizes (13 nm, 38 nm, and <1 µm) at four different values of average electric field Eav (0.0 Vmm−1, 125 Vmm−1, 250 Vmm−1, and 500 Vmm−1) for 1 h each. Changes in selected dielectric parameters (dielectric constant εr and dielectric loss factor tanδ) of the composites were analyzed using broadband dielectric spectroscopy (10−1 Hz to 105 Hz). The influence of the Eav and the current i(t) flowing through the sample material and the Joule heat generated in it on the resin curing process and the final gradient of dielectric parameters were investigated. The results show that the degree of modification of the εr gradient increases with increasing Eav and is more pronounced in the case of TiO2 nanoparticles. The largest modifications in the εr and tanδ were obtained for nanoparticles with a diameter of 13 nm at Eav = 500 Vmm−1, while the lowest for particles < 1 µm at Eav = 125 Vmm−1. The effect of electrophoresis on the dielectric parameters is significant, especially near the anode region. Increasing the concentration of TiO2 particles at the anode occurs at the expense of reducing their concentration in the remaining volume of the sample. The test results clearly demonstrate the importance of particle dimension and electric field strength for the gradient modification of the properties of the epoxy composite using electrophoresis. Numerical simulations of electric field stresses in the epoxy resin during the electrophoresis process, performed in the COMSOL program, revealed a significant increase in the E field strength in the areas close to the anode and cathode. [ABSTRACT FROM AUTHOR]

Silver nanoparticles were synthesized via laser ablation in two different organic solvents (tetrahydrofuran and toluene). The influence of solvent choice on the production and behavior of silver nanoparticles dispersed in a polystyrene matrix was investigated. UV–Vis spectroscopy, ellipsometry and scanning probe microscopy techniques were used for characterization. The silver nanoparticles' optical properties were modified by the existence of a core-shell structure appearing in toluene-ablated particles. For both solvents and, in particular, for the toluene case, the particles showed good dispersion in the matrix. Additionally, the interphase behavior of the doped polymer films was influenced by the synthesis process, affecting the mechanical and optical (dielectric) properties. The observed results for the nanocomposite are attributed to the formation of a core-shell structure around the particles directly due to the ablation in organic solvents. These findings contribute to the understanding of silver/polystyrene nanocomposites and offer opportunities for developing tailored functional materials by using laser ablation in liquids. [ABSTRACT FROM AUTHOR]

The paper presents the effects of gradual temperature curing on the dielectric properties of epoxy nanocomposite samples. Samples were prepared based on Class H epoxy resin filled with nano-alumina (Al2O3) for different wt% loadings (0.5 wt% to 5.0 wt%) and two different filler sizes (13 nm and <50 nm), i.e., two different specific surface area values. During the research, specimen sets were cured gradually at increasingly higher temperatures (from 60 °C to 180 °C). Broadband dielectric spectroscopy (BDS) was used to determine the characteristics of the dielectric constant and the dielectric loss factor in the frequency range from 10−3 Hz to 105 Hz. As a result, it was possible to analyze the impact of the progressing polymer structure thermosetting processes on the observed dielectric parameters of the samples. The nano-Al2O3 addition with 0.5 wt%, 1.0 wt%, and 3.0 wt% resulted in a decrease in dielectric constant values compared to neat epoxy resin samples. The most significant reductions were recorded for samples filled with 0.5 wt% of 13 nm and <50 nm powders, by about 15% and 11%, respectively. For all tested samples, the curing process at a gradually higher temperature caused a slight decrease in the dielectric constant (approx. 2% to 9%) in the whole frequency range. Depending on the nanofiller content and the curing stage, the dielectric loss factor of the nanocomposite may be lower or higher than that of the neat resin. For all tested samples cured at 130 °C (and post-cured at 180 °C), the differences in the dielectric loss factor characteristics for frequencies greater than 100 Hz are low. For frequencies < 100 Hz, there are prominent differences in the characteristics related to the size of the nanoparticle and the individual wt% value. At a small nanofiller amount (0.5 wt%), a decrease in the dielectric constant and dielectric loss factor was observed for frequencies < 100 Hz for samples with nanofillers of both sizes. [ABSTRACT FROM AUTHOR]