Search

In the recent times, pseudocapacitive electrode materials have received great attention due to their considerable capability in storing ions at relatively fast charging rates. Among various candidates, niobium (V) pentoxide (Nb 2 O 5 ) has gained much attraction for lithium-ion batteries (LIBs) due to its insertion/extraction reaction with Li, safe redox potential, and considerably good capacity (about 200 mAhg −1 ). Nevertheless, low conductivity of Nb 2 O 5 has so far prevented its use as a viable electrode material for LIBs. In this study, we have successfully coated silver (Ag) nanoparticles (NPs) on the surface of one-dimensional orthorhombic Nb 2 O 5 fiber (1D T-Nb 2 O 5 ) using simple electrospinning processing. Ag NPs coated Nb 2 O 5 fibers (Ag-1D T-Nb 2 O 5 ) provided faster electron pathways, resulting in much improved capacity at a given current density with superior rate capabilities compared with pristine 1D T-Nb 2 O 5 . In addition, 1D T-Nb 2 O 5 was more suitable for coating Ag NPs compared with T-Nb 2 O 5 NPs, where its structural integrity was maintained even after cycling. As a result, effective coating of conductive Ag NPs on the 1D T-Nb 2 O 5 resulted in excellent cycle retention characteristics (179.7 mAhg −1 after 500 cycles at 500 mA g −1 ) as well as superior rate capabilities (103.6 mAhg −1 at a current density of 5000 mA g −1 ). [ABSTRACT FROM AUTHOR]

Structural and electronic modification of titanium oxide (TiO 2 ) nanomaterials induced by the co-introduction of fully disordered glass phase and oxygen vacancies can lead to remarkable advances in the electrode performance in emerging energy storage systems. We report on the effective co-creation of fully amorphous nanofibers (NFs) composed of black TiO 2-x and conductive carbons throughout the NF structure, and evaluate the materials as potential anodes in sodium-ion batteries. The black TiO 2-x nanofiber is successfully fabricated by electrospinning a precursor solution followed by a two-step sequential thermal treatment in an air and reducing atmosphere. The NF electrode could deliver approximately two-fold higher 2nd discharge capacity and an excellent kinetic performance even under high rates compared to that delivered by anatase-structured white TiO 2 NFs used as reference, because of (i) an inherent free volume in the glass phase corresponding to the enlarged Na + sites, (ii) increased electrical conductivity (low bandgap) resulting from the presence of Ti 3+ , (iii) introduction of conductive carbon agents around the TiO 2-x domain, and (iv) one-dimensional NF feature allowing numerous Na + reaction sites at the electrochemical interface. We also elucidate the morphological and structural changes in the nanofibers after discharge and charge by ex-situ characterizations. [ABSTRACT FROM AUTHOR]

• Synthesis of CA-CNF by insulating block electrospinning & carbonization. • Formation of cross-aligned network even after heat treatment. • Faster reaction kinetics and regular electron pathway of CA-CNF. • High-rate cyclability of CA-CNF (259.4 mAh g−1 at 3000 mA g−1). The conventional use of metallic current collector in an electrochemical cell results in decreased loading of active materials and hence limited capacity in consideration of all the inactive current collector components. In response to this trend, a number of conductive, free-standing materials have been proposed as electrodes, which would act as both current collector and active materials. Here, in this study, we have firstly developed the cross-aligned carbon nanofiber (CA-CNF) for efficient Li storage, especially at high current densities. Using the insulating block electrospinning, the nanofibers can be aligned in a certain direction, where it is viable to fabricate cross-aligned nanofibers in a cost-effective and scalable manner. Attributed to faster kinetics and regular electron pathway arising from CA-CNF, it exhibits an excellent high-rate cyclability (259.4 mAh g−1 at a current density of 3000 mA g−1). This work builds up a milestone in suggesting a cross-aligned carbon nanofibrous network as efficient Li storage, which can also be applied to various electrode materials embedded cross-aligned conductive composite materials. [Display omitted] [ABSTRACT FROM AUTHOR]